PA12 UBE JAPAN 3030JI5L

Extrusion grade

US$ 10,540 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	UBE JAPAN/3030JI5L
bending strength		ISO 178	19.0 Mpa
Charpy Notched Impact Strength	-40℃	ISO 179/1eA	4C KJ/m
Tensile strain	Break	ISO 527-2	200 %
Elongation at Break		ASTM D412/ISO 527	＞200 %
Rockwell hardness		ISO 2039-2	51 R
Tensile strain	Yield	ISO 527-2	24 %
tensile strength		ASTM D412/ISO 527	26 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	19 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength	23℃	ISO 179/1eA	115P KJ/m
elongation	Break	ISO 527-1/-2	＞200 %
Shore hardness		ISO 868	67 D
tensile strength	Yield	ISO 527-2	26.0 Mpa
Rockwell hardness		ASTM D785	51
tensile strength	Yield	ISO 527-1/-2	26 Mpa
Bending modulus		ISO 178	400 Mpa
Bending modulus			ASTM D412/ISO 527	400 kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	UBE JAPAN/3030JI5L
Melting temperature		ISO 3146	173 °C
Hot deformation temperature	HDT	ASTM D648/ISO 75	91 ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	1.7 mm/mm.℃
Hot deformation temperature	0.45Mpa	ISO 75-2	91 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.7E-04 cm/cm/°C
Hot deformation temperature	1.8Mpa	ISO 75-2	45 °C
Hot deformation temperature		0.45MPa,Unannealed	ISO 75-2/B	91.0 °C
Linear coefficient of thermal expansion		ISO 11359-2	1.7
Melting temperature			173 ℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	45.0 °C
Physical properties	Test Condition	Test Method	UBE JAPAN/3030JI5L
Water absorption rate	23°C,24hr	ISO 62	0.60 %
Shrinkage rate		ISO 294-4	0.7/1.4 %
		MD	ISO 294-4	0.70 %
			ASTM D955	0.7/1.4 %
melt mass-flow rate		ASTM D1238/ISO 1133	4 g/10min
		235°C/2.16kg	ISO 1133	4.0 g/10min
			ISO 1133	4 g/10min
Melting temperature		ISO 11357-3	173 °C
Water absorption rate		ISO 62	0.6 %
Shrinkage rate	TD	ISO 294-4	1.4 %
density		ASTM D792/ISO 1183	1.01 kg·cm/cm(J/M)ft·lb/in
Electrical performance	Test Condition	Test Method	UBE JAPAN/3030JI5L
Volume resistivity		IEC 60093	1E+12 Ω.cm
Volume resistivity			ASTM D257/IEC 60093	1012 Ω.cm
hardness	Test Condition	Test Method	UBE JAPAN/3030JI5L
Rockwell hardness	R-Sale	ISO 2039-2	51
Shore hardness	ShoreD	ISO 868	67