'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA12 3030JI5L UBE JAPAN
159
Form：Granules | Grade：Extrusion grade
Properties:
Good flexibilityHigh impact resistanceheat-resistingToughening
Typical Applications:
Pipe fittingsAutomotive sectorPipe fittings
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Pipe fittings | Automotive sector | Pipe fittings |
| Properties: | Good flexibility | High impact resistance | heat-resisting | Toughening |
Certificates
No Data...
Technical Data Sheet
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 19 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D412/ISO 527 | 400 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 51 | ||
| tensile strength | ASTM D412/ISO 527 | 26 | kg/cm²(MPa)[Lb/in²] | |
| Elongation at Break | ASTM D412/ISO 527 | ＞200 | % | |
| Charpy Notched Impact Strength | -40℃ | ISO 179/1eA | 4C | KJ/m |
| 23℃ | ISO 179/1eA | 115P | KJ/m | |
| Rockwell hardness | ISO 2039-2 | 51 | R | |
| Shore hardness | ISO 868 | 67 | D | |
| Bending modulus | ISO 178 | 400 | Mpa | |
| bending strength | ISO 178 | 19 | Mpa | |
| elongation | Break | ISO 527-1/-2 | ＞200 | % |
| tensile strength | Yield | ISO 527-1/-2 | 26 | Mpa |
| Bending modulus | ISO 178 | 400 | Mpa | |
| bending strength | ISO 178 | 19.0 | Mpa | |
| tensile strength | Yield | ISO 527-2 | 26.0 | Mpa |
| Tensile strain | Yield | ISO 527-2 | 24 | % |
| Break | ISO 527-2 | 200 | % | |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | 173 | ℃（℉） | ||
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 45 | ℃（℉） |
| HDT | ASTM D648/ISO 75 | 91 | ℃（℉） | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1.7 | ||
| Hot deformation temperature | 1.8Mpa | ISO 75-2 | 45 | °C |
| 0.45Mpa | ISO 75-2 | 91 | °C | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.7 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO 75-2/B | 91.0 | °C |
| 1.8MPa,Unannealed | ISO 75-2/A | 45.0 | °C | |
| Melting temperature | ISO 3146 | 173 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.7E-04 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Melting temperature | ISO 11357-3 | 173 | °C | |
| melt mass-flow rate | ISO 1133 | 4 | g/10min | |
| Water absorption rate | ISO 62 | 0.6 | % | |
| Shrinkage rate | ISO 294-4 | 0.7/1.4 | % | |
| density | ASTM D792/ISO 1183 | 1.01 | kg·cm/cm(J/M)ft·lb/in | |
| Shrinkage rate | ASTM D955 | 0.7/1.4 | % | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 4 | g/10min | |
| 235°C/2.16kg | ISO 1133 | 4.0 | g/10min | |
| Shrinkage rate | TD | ISO 294-4 | 1.4 | % |
| MD | ISO 294-4 | 0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | ASTM D257/IEC 60093 | 1012 | Ω.cm | |
| IEC 60093 | 10 | Ω.cm | ||
| IEC 60093 | 1E+12 | ohms·cm | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale | ISO 2039-2 | 51 | |
| Shore hardness | ShoreD | ISO 868 | 67 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.