PPS 1130A1 PPS vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PPS JAPAN POLYPLASTIC 1130A1

Injection grade

ULSGS

US$ 6,570 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
Dielectric strength	3.00mm	IEC 60243-1	16 KV/mm
Dissipation factor	1kHz	IEC 60250	1E-03
Dielectric loss	3mmt	IEC 60243-1	16 KV/mm
Dissipation factor	耐电弧性	IEC 60250	124 sec
Relative permittivity	1kHz	IEC 60250	4.00
Compared to the anti leakage trace index		IEC 60112	PLC 4
Volume resistivity		IEC 60093	3×1016 ohms·cm
Leakage Tracking Index (CTI)		IEC 60112	150 V
Volume resistivity		ASTM D257/IEC 60093	3.0 x 10^16 Ω.cm
Dissipation factor	1MHz	IEC 60250	2E-03
Surface resistivity		IEC 60093	2×1017 Ω
Relative permittivity	1MHz	IEC 60250	4.00
mechanical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
bending strength		ISO 178	245 Mpa
Fracture strain		ISO 527-1	2 %
Tensile strain	Break	ISO 527-2	2.0 %
tensile strength		ISO 527-1	170 Mpa
bending strength		ASTM D790/ISO 178	245 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2 %
Bending modulus		ISO 178	10000 Mpa
tensile strength		ISO 527-2	170 Mpa
tensile strength			ASTM D638/ISO 527	170 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	10000 kg/cm²(MPa)[Lb/in²]
Charpy Notched Impact Strength		ISO 179/1eA	10.0 kJ/m²
Physical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
Water absorption rate		ASTM D570/ISO 62	0.01 %
Water absorption rate		23°C,24hr	ISO 62	0.030 %
Shrinkage rate	Across Flow，80℃×2mmt		0.6 %
Shrinkage rate		Flow，80℃×2mmt		0.3 %
Melt viscosity	310°C,1000sec^-1	ISO 11443	350000 mPa·s
density		ASTM D792/ISO 1183	1.57
Supplementary Information	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
ColourNumber			HF2000/HD9050
Basic Performance	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
Water absorption rate	23℃,水中24hr	ISO 62	0.01 %
density		ISO 1183	1.57 g/cm³
Melt viscosity	310℃,1000/sec	ISO 11443	350 Pa·s
thermal performance	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
Linear coefficient of thermal expansion	MD	Internal Method	2E-05 cm/cm/°C
		Flow	ISO 11359-2	2 ×10-5/℃
		Across Flow		4 ×10-5/℃
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260 °C
Hot deformation temperature		1.8MPa	ISO 75-1	260 °C
Linear coefficient of thermal expansion	TD	Internal Method	4E-05 cm/cm/°C
flammability	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
UL flame retardant rating		UL 94	V-0
hardness	Test Condition	Test Method	JAPAN POLYPLASTIC/1130A1
Rockwell hardness	M-Scale	ISO 2039-2	105

Supplier Join

Get App

Top