PPS 1130A1 JAPAN POLYPLASTIC

293

Form：Granules | Grade：Injection grade

Properties:

high strengthHigh temperature resistanHigh toughnessFlame retardantenhance

Typical Applications:

Household appliancesHousehold appliancesFitness equipmentAutomotive sectorBottle cap

Supplier(3)

Product Description

Certificates(2)

Datasheet

Product Description

Typical Applications:	Household appliances \| Household appliances \| Fitness equipment \| Automotive sector \| Bottle cap
Properties:	high strength \| High temperature resistan \| High toughness \| Flame retardant \| enhance

Certificates

SGS

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.57	g/cm³
Melt viscosity	310℃,1000/sec	ISO 11443	350	Pa·s
Water absorption rate	23℃,水中24hr	ISO 62	0.01	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ASTM D638/ISO 527	170	kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	10000	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	245	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2	%
tensile strength		ISO 527-1	170	Mpa
Fracture strain		ISO 527-1	2	%
tensile strength		ISO 527-2	170	Mpa
Tensile strain	Break	ISO 527-2	2.0	%
Bending modulus		ISO 178	10000	Mpa
bending strength		ISO 178	245	Mpa
bending strength	bending strength		ISO 178	245	Mpa
Bending modulus		ISO 178	10000	Mpa
Charpy Notched Impact Strength		ISO 179/1eA	10.0	kJ/m²
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
Linear coefficient of thermal expansion	MD	Internal Method	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	Internal Method	4E-05	cm/cm/°C
Hot deformation temperature	1.8MPa	ISO 75-1	260	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2	×10-5/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow		4	×10-5/℃
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D792/ISO 1183	1.57
Water absorption rate		ASTM D570/ISO 62	0.01	%
Shrinkage rate	Flow，80℃×2mmt		0.3	%
Shrinkage rate	Shrinkage rate	Across Flow，80℃×2mmt		0.6	%
Melt viscosity	310°C,1000sec^-1	ISO 11443	350000	mPa·s
Water absorption rate	23°C,24hr	ISO 62	0.030	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	3.0 x 10^16	Ω.cm
Volume resistivity	Volume resistivity		IEC 60093	3E+16	ohms·cm
Dielectric strength	3.00mm	IEC 60243-1	16	KV/mm
Relative permittivity	1kHz	IEC 60250	4.00
Relative permittivity	Relative permittivity	1MHz	IEC 60250	4.00
Dissipation factor	1kHz	IEC 60250	1E-03
	Dissipation factor	1MHz	IEC 60250	2E-03
	Dissipation factor	Dissipation factor	耐电弧性	IEC 60250	124	sec
Compared to the anti leakage trace index		IEC 60112	PLC 4
Volume resistivity		IEC 60093	3×1016	Ω·cm
Dielectric loss	3mmt	IEC 60243-1	16	KV/mm
Surface resistivity		IEC 60093	2×1017	Ω
Leakage Tracking Index (CTI)		IEC 60112	150	V
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	105
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			HF2000/HD9050

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PPS 1130A1 JAPAN POLYPLASTIC

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index