PA46 TW363 PA46 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA46 DSM HOLAND TW363

Extrusion grade

US$ 7,110 / MT

FOB Guangzhou port, China

thermal performance	Test Condition	Test Method	DSM HOLAND/TW363
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.8E-4 cm/cm/°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	200 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	90.0 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	1.6E-4 cm/cm/°C
Thermal Index - 5000 hr		IEC 60216	135 °C
Melting temperature		ISO 11357-3	295 °C
mechanical properties	Test Condition	Test Method	DSM HOLAND/TW363
tensile strength	Yield, 120°C	ISO 527-2	35.0 Mpa
tensile strength		Yield, 160°C	ISO 527-2	30.0 Mpa
Bending modulus	--	ISO 178	1800 Mpa
Tensile modulus	--	ISO 527-2	1850 Mpa
Nominal tensile fracture strain	--	ISO 527-2	> 50 %
tensile strength	Yield	ISO 527-2	60.0 Mpa
Nominal tensile fracture strain	160°C	ISO 527-2	> 50 %
Nominal tensile fracture strain		120°C	ISO 527-2	> 50 %
Tensile modulus	120°C	ISO 527-2	400 Mpa
Bending modulus	160°C	ISO 178	350 Mpa
Bending modulus		120°C	ISO 178	400 Mpa
Tensile modulus	160°C	ISO 527-2	350 Mpa
Physical properties	Test Condition	Test Method	DSM HOLAND/TW363
density		ISO 1183	1.10 g/cm³
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	3.0 %
Shrinkage rate	Flow	ISO 294-4	2.0 %
Shrinkage rate		横向Flow	ISO 294-4	2.0 %
impact performance	Test Condition	Test Method	DSM HOLAND/TW363
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	26 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	80 kJ/m²
Impact strength of cantilever beam gap		-40°C	ISO 180/1A	40 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	75 kJ/m²
Electrical performance	Test Condition	Test Method	DSM HOLAND/TW363
Compared to the anti leakage trace index		IEC 60112	PLC 1
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Relative permittivity	100 Hz	IEC 60250	3.60
Relative permittivity		1 MHz	IEC 60250	3.20
Dielectric strength		IEC 60243-1	25 KV/mm