PC
PC SABIC INNOVATIVE US 144R-111
Injection grade
US$ 2,822 / MT
FOB Guangzhou port, China
injectionTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
Back pressure0.300 to 0.700 Mpa
Temperature at the front of the material cylinder295 to 315 °C
Screw speed40 to 70 rpm
Mold temperature70 to 95 °C
Processing (melt) temperature295 to 315 °C
Suggested injection volume40 to 60 %
Suggested maximum moisture content0.020 %
Spray nozzle temperature290 to 310 °C
Exhaust hole depth0.025 to 0.076 mm
drying temperature120 °C
Temperature in the middle of the barrel280 to 305 °C
drying time3.0 to 4.0 hr
Temperature at the rear of the barrel270 to 295 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
bending strength--5,6ISO 17890.0 Mpa
Bending modulus50.0 mm Span4ASTM D7902340 Mpa
bending strengthYield, 50.0 mm Span4ASTM D79097.0 Mpa
elongationBreakISO 527-2/50110 %
Yield3ASTM D6387.0 %
YieldISO 527-2/506.0 %
Taber abraser1000 Cycles, 1000 g, CS-17 WheelASTM D104410.0 mg
elongationBreak3ASTM D638130 %
tensile strengthBreakISO 527-2/5070.0 Mpa
YieldISO 527-2/5063.0 Mpa
Yield3ASTM D63862.0 Mpa
Tensile modulus--2ASTM D6382370 Mpa
--ISO 527-2/12350 Mpa
Bending modulus--5ISO 1782300 Mpa
tensile strengthBreak3ASTM D63868.0 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
Hot deformation temperature0.45 MPa, Unannealed, 6.40 mmASTM D648137 °C
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10ISO 75-2/Ae125 °C
Vicat softening temperature--ASTM D152511154 °C
thermal conductivity--ISO 83020.20 W/m/K
Linear coefficient of thermal expansion-40 to 95°C，FlowASTM E8316.8E-5 cm/cm/°C
Hot deformation temperature0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10ISO 75-2/Be136 °C
specific heatASTM C3511250 J/kg/°C
thermal conductivity--ASTM C1770.19 W/m/K
Vicat softening temperature--ISO 306/B50141 °C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D648132 °C
RTI ElecUL 746130 °C
RTI ImpUL 746130 °C
Vicat softening temperature--ISO 306/A50153 °C
RTIUL 746130 °C
Linear coefficient of thermal expansion23 to 80°C，FlowISO 11359-27.0E-5 cm/cm/°C
Vicat softening temperature--ISO 306/B120142 °C
Ball Pressure Test123 to 127°CIEC 60695-10-2通过
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
Dart impact23°CASTM D3029169 J
Suspended wall beam without notch impact strength23°CASTM D48123200 J/m
Dart impact23°C, Energy at PeakASTM D376363.0 J
Impact strength of cantilever beam gapASTM D1822577 kJ/m²
optical performanceTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
turbidity2540 μmASTM D10031.0 %
transmissivity2540 μmASTM D100388.0 %
Refractive indexASTM D5421.586
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
Extreme Oxygen IndexASTM D286325 %
UL flame retardant rating1.5 mmUL 94HB
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
Compared to the anti leakage trace indexUL 746PLC 2
Dissipation factor50 HzASTM D1509.0E-4
60 HzASTM D1509.0E-4
1 MHzASTM D1500.010
Dielectric strength3.20 mm, in OilIEC 60243-117 KV/mm
High voltage arc tracing rateUL 746PLC 2
Dielectric constant60 HzIEC 602502.70
Surface resistivityIEC 60093> 1.0E+15 ohms
Dielectric constant50 HzIEC 602502.70
1 MHzASTM D1502.96
Volume resistivity--IEC 60093> 1.0E+15 ohms·cm
Dielectric strength3.20 mm, in AirASTM D14915 KV/mm
Dissipation factor50 HzIEC 602501.0E-3
Volume resistivity--ASTM D257> 1.0E+17 ohms·cm
High arc combustion indexUL 746PLC 1
Hot wire ignitionUL 746PLC 2
Dissipation factor60 HzIEC 602501.0E-3
Dielectric constant60 HzASTM D1503.17
50 kHzASTM D1503.17
1 MHzIEC 602502.70
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
Rockwell hardnessR-ScaleASTM D785118
M-ScaleASTM D78570
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/144R-111
Melt Volume Flow Rate (MVR)300°C/1.2 kgISO 113310.0 cm3/10min
Water absorption rate24 hrASTM D5700.15 %
Equilibrium, 100°CASTM D5700.58 %
Specific volumeASTM D7920.830 cm³/g
Water absorption rateEquilibrium, 23°CASTM D5700.35 %
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.70 %
melt mass-flow rate300°C/1.2 kgASTM D123811 g/10 min