PC 144R-111 SABIC INNOVATIVE US

113

Form：Granules | Grade：Injection grade

Properties:

Flame retardanttransparent

Typical Applications:

Medical suppliesNursing suppliesNon specific food

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Medical supplies \| Nursing supplies \| Non specific food
Properties:	Flame retardant \| transparent

Certificates

No Data...

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.586
transmissivity	2540 μm	ASTM D1003	88.0	%
turbidity	2540 μm	ASTM D1003	1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200	J/m
Dart impact	23°C, Energy at Peak	ASTM D3763	63.0	J
Dart impact	Dart impact	23°C	ASTM D3029	169	J
Impact strength of cantilever beam gap		ASTM D1822	577	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
Extreme Oxygen Index		ASTM D2863	25	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	ASTM D1044	10.0	mg
bending strength	Yield, 50.0 mm Span4	ASTM D790	97.0	Mpa
bending strength	bending strength	--5,6	ISO 178	90.0	Mpa
Bending modulus	--5	ISO 178	2300	Mpa
Bending modulus	Bending modulus	50.0 mm Span4	ASTM D790	2340	Mpa
elongation	Break	ISO 527-2/50	110	%
	elongation	Break3	ASTM D638	130	%
		elongation	Yield	ISO 527-2/50	6.0	%
		elongation	elongation	Yield3	ASTM D638	7.0	%
tensile strength	Break	ISO 527-2/50	70.0	Mpa
	tensile strength	Break3	ASTM D638	68.0	Mpa
		tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	62.0	Mpa
Tensile modulus	--	ISO 527-2/1	2350	Mpa
Tensile modulus	Tensile modulus	--2	ASTM D638	2370	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Back pressure			0.300 to 0.700	Mpa
Temperature at the front of the material cylinder			295 to 315	°C
Spray nozzle temperature			290 to 310	°C
Processing (melt) temperature			295 to 315	°C
Mold temperature			70 to 95	°C
drying temperature			120	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.020	%
Suggested injection volume			40 to 60	%
Temperature at the rear of the barrel			270 to 295	°C
Temperature in the middle of the barrel			280 to 305	°C
Screw speed			40 to 70	rpm
Exhaust hole depth			0.025 to 0.076	mm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	-40 to 95°C，Flow	ASTM E831	6.8E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	23 to 80°C，Flow	ISO 11359-2	7.0E-5	cm/cm/°C
specific heat		ASTM C351	1250	J/kg/°C
thermal conductivity	--	ASTM C177	0.19	W/m/K
thermal conductivity	thermal conductivity	--	ISO 8302	0.20	W/m/K
RTI Elec		UL 746	130	°C
RTI Imp		UL 746	130	°C
RTI		UL 746	130	°C
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	136	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	132	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	125	°C
Vicat softening temperature	--	ASTM D152511	154	°C
	Vicat softening temperature	--	ISO 306/A50	153	°C
		Vicat softening temperature	--	ISO 306/B50	141	°C
		Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	142	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	11	g/10 min
Specific volume		ASTM D792	0.830	cm³/g
Water absorption rate	Equilibrium, 100°C	ASTM D570	0.58	%
	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.35	%
	Water absorption rate	Water absorption rate	24 hr	ASTM D570	0.15	%
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70	%
Melt Volume Flow Rate (MVR)	300°C/1.2 kg	ISO 1133	10.0	cm3/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	60 Hz	ASTM D150	3.17
	Dielectric constant	60 Hz	IEC 60250	2.70
	Dielectric constant	Dielectric constant	50 kHz	ASTM D150	3.17
Dielectric strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Dielectric constant	1 MHz	ASTM D150	2.96
Dielectric constant	Dielectric constant	50 Hz	IEC 60250	2.70
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity	--	ASTM D257	> 1.0E+17	ohms·cm
Volume resistivity	Volume resistivity	--	IEC 60093	> 1.0E+15	ohms·cm
Dielectric strength	3.20 mm, in Air	ASTM D149	15	KV/mm
Dielectric constant	1 MHz	IEC 60250	2.70
Dissipation factor	50 Hz	ASTM D150	9.0E-4
	Dissipation factor	60 Hz	ASTM D150	9.0E-4
		Dissipation factor	1 MHz	ASTM D150	0.010
			Dissipation factor	50 Hz	IEC 60250	1.0E-3
			Dissipation factor	Dissipation factor	60 Hz	IEC 60250	1.0E-3
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 2
Hot wire ignition		UL 746	PLC 2
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	70

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC 144R-111 SABIC INNOVATIVE US

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index