PA612
PA612 DUPONT USA 77G43L NC010
Injection grade
US$ 5,859 / MT
FOB Guangzhou port, China
Physical propertiesTest ConditionTest MethodDUPONT USA/77G43L NC010
Water absorption rateSaturation, 23°C, 2.00 mmISO 621.7 %
Shrinkage rateFlowISO 294-40.30 %
横向FlowISO 294-40.80 %
Water absorption rateEquilibrium, 23°C, 2.00 mm, 50% RHISO 620.70 %
StickinessISO 307145 cm³/g
flammabilityTest ConditionTest MethodDUPONT USA/77G43L NC010
雾化 - G-value (condensate)ISO 64521.0E-4 g
FMVSS combustion rateFMVSS 302B
Burning rate1.00 mmISO 379521 mm/min
UL flame retardant ratingUL 94HB
thermal performanceTest ConditionTest MethodDUPONT USA/77G43L NC010
Linear coefficient of thermal expansionAcross FlowISO 11359-21.1E-4 cm/cm/°C
Hot deformation temperature0.45 MPa, UnannealedISO 75-2/B217 °C
1.8 MPa, UnannealedISO 75-2/A203 °C
Linear coefficient of thermal expansionFlowISO 11359-21.4E-5 cm/cm/°C
Flow : -40 to 23°CISO 11359-22.1E-5 cm/cm/°C
Across Flow : -40 to 23°CISO 11359-27.5E-5 cm/cm/°C
Across Flow : 55 to 160°CISO 11359-21.4E-4 cm/cm/°C
Glass transition temperatureISO 11357-265.0 °C
Linear coefficient of thermal expansionFlow : 55 to 160°CISO 11359-21.3E-5 cm/cm/°C
Melting temperatureISO 11357-3218 °C
injectionTest ConditionTest MethodDUPONT USA/77G43L NC010
Melt Temperature, Optimum290 °C
Hold Pressure Time3.00 s/mm
Mold temperature70 to 120 °C
Processing (melt) temperature280 to 300 °C
drying temperature80 °C
Maximum Screw Tangential Speed12 m/min
Mold Temperature, Optimum100 °C
Maintain pressure50.0 to 100 Mpa
Drying Recommendedyes
Drying time - hot air dryer2.0 to 4.0 hr
Suggested maximum moisture content0.20 %
mechanical propertiesTest ConditionTest MethodDUPONT USA/77G43L NC010
Tensile strainBreakISO 527-23.0 %
tensile strengthBreakISO 527-2200 Mpa
Tensile modulusISO 527-212500 Mpa
Bending modulusISO 17811000 Mpa
impact performanceTest ConditionTest MethodDUPONT USA/77G43L NC010
Impact strength of simply supported beam without notch23°CISO 179/1eU100 kJ/m²
-30°CISO 179/1eU85 kJ/m²
hardnessTest ConditionTest MethodDUPONT USA/77G43L NC010
Rockwell hardnessR -SaleISO 2039-2118
Filling analysisTest ConditionTest MethodDUPONT USA/77G43L NC010
Top out temperature210 °C
Electrical performanceTest ConditionTest MethodDUPONT USA/77G43L NC010
Volume resistivityIEC 62631-3-11.0E+13 ohms·m