Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Shrinkage rate | | ISO 294-4 | 0.80 % |
| Shrinkage rate | | ISO 294-4 | 0.30 % |
| Water absorption rate | | ISO 62 | 1.7 % |
| Water absorption rate | | ISO 62 | 0.70 % |
| viscosity number | | ISO 307 | 145 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | ISO 2039-2 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| burning rate | | ISO 3795 | 21 mm/min |
| UL flame retardant rating | | UL 94 | HB |
| UL flame retardant rating | | UL 94 | HB |
| FMVSS combustion rate | | FMVSS 302 | B |
| | ISO 6452 | 1.0E-4 g |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 12500 Mpa |
| tensile strength | | ISO 527-2 | 200 Mpa |
| Tensile strain | | ISO 527-2 | 3.0 % |
| Flexural modulus | | ISO 178 | 11000 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 85 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 100 kJ/m² |
| Filling analysis | Test Condition | Test Method | Test Result |
|---|
| Ejection Temperature | | | 210 °C |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | IEC 62631-3-1 | 1.0E+13 ohms·m |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 80 °C |
| Drying time - hot air dryer | | | 2.0 to 4.0 hr |
| Suggested maximum moisture content | | | 0.20 % |
| Processing (melt) temperature | | | 280 to 300 °C |
| Melt Temperature, Optimum | | | 290 °C |
| Temperature | | | 70 to 120 °C |
| Mold Temperature, Optimum | | | 100 °C |
| pressure holding | | | 50.0 to 100 Mpa |
| pressure holding | | | yes |
| Hold Pressure Time | | | 3.00 s/mm |
| Maximum Screw Tangential Speed | | | 12 m/min |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Hot deformation temperature (HDT) | | ISO 75-2/B | 217 °C |
| Hot deformation temperature (HDT) | | ISO 75-2/A | 203 °C |
| Glass Transition Temperature | | ISO 11357-2 | 65.0 °C |
| melting temperature | | ISO 11357-3 | 218 °C |
| | ISO 11359-2 | 1.4E-5 cm/cm/°C |
| | ISO 11359-2 | 2.1E-5 cm/cm/°C |
| | ISO 11359-2 | 1.3E-5 cm/cm/°C |
| | ISO 11359-2 | 1.1E-4 cm/cm/°C |
| | ISO 11359-2 | 7.5E-5 cm/cm/°C |
| | ISO 11359-2 | 1.4E-4 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.