PA66 1300G PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 ASAHI JAPAN 1300G

Enhanced level

US$ 3,240 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	ASAHI JAPAN/1300G
elongation	Break	ASTM D638	3.0 %
Rockwell hardness	干(湿)	ASTM D-785	96(75) R scale
bending strength	23°C	ISO 178	275 Mpa
tensile strength		ASTM D638	186 Mpa
bending strength	干(湿)	ASTM D-790	289(216) Mpa
bending strength			ASTM D790/ISO 178	289(MPa) kg·cm/cm(J/M)ft·lb/in
Rockwell hardness		ASTM D785	M96
Bending modulus		ASTM D790/ISO 178	9320(MPa) kg·cm/cm(J/M)ft·lb/in
Tensile modulus	23°C	ISO 527-2	10000 Mpa
Tensile strain	Break,23°C	ISO 527-2	3.0 %
Taber abraser	1000Cycles	ASTM D1044	-- mg
tensile strength	Break,23°C	ISO 527-2	190 Mpa
bending strength		ASTM D790	289 Mpa
tensile strength	干(湿)	ASTM D-638	186(132) Mpa
flexural coefficient	干(湿)	ASTM D-790	9.3(6.3) GPa
Impact strength of cantilever beam gap	干(湿)	ASTM D-256	127(147) J/m
Bending modulus	23°C	ISO 178	9000 Mpa
Bending modulus			ASTM D790	9300 Mpa
Elongation at Break	干(湿)	ASTM D-638	3(5) %
other	Test Condition	Test Method	ASAHI JAPAN/1300G
characteristic			高刚性
Electrical performance	Test Condition	Test Method	ASAHI JAPAN/1300G
Arc resistance		ASTM D495/IEC 60112	124
Volume resistivity	23°C	IEC 60093	1E+15 ohms·cm
Surface resistivity		ASTM D257	1E+15 ohms
Surface resistivity			IEC 60093	1E+15 ohms
Dielectric strength		IEC 60243-1	28 KV/mm
Dielectric strength			ASTM D149	28 KV/mm
Compared to the anti leakage trace index	3.00mm	IEC 60112	PLC 0
Volume resistivity		ASTM D257	1E+15 ohms·cm
Physical properties	Test Condition	Test Method	ASAHI JAPAN/1300G
Shrinkage rate	吸水率(Saturation,23°C)	Internal Method	-- %
		干	旭化成方法	0.4/0.9 %
			ASTM D955	0.4-0.9 %
		MD	Internal Method	0.40 %
density		ASTM D792/ISO 1183	1.39
Water absorption rate		ASTM D570/ISO 62	1.7 %
Wear factor	湿	ASTM D-1044	15 ×10-6kg/1000times
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	-- %
Shrinkage rate	TD	Internal Method	0.90 %
thermal performance	Test Condition	Test Method	ASAHI JAPAN/1300G
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	3 mm/mm.℃
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	260 °C
UL flame retardant rating	干	UL 94	HB
thermal conductivity			0.30 W/m/K
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	250 °C
		HDT	ASTM D648/ISO 75	250 ℃（℉）
		0.46MPa,干	ASTM D-648	260 °C
		1.82MPa,干	ASTM D-648	250 °C
specific heat			1590 J/kg/°C
Linear coefficient of thermal expansion	MD	ASTM D696	3E-05 cm/cm/°C
thermal conductivity	干		0.3 W/(m.K)
Linear coefficient of thermal expansion	干	ASTM D-696	3 ×10-5/K
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	265 °C
Hot deformation temperature		1.8MPa,Unannealed	ASTM D648	250 °C
Combustibility (rate)		UL 94	HB
specific heat	干		1590 J/(kg.k)
flammability	Test Condition	Test Method	ASAHI JAPAN/1300G
Extreme Oxygen Index		ASTM D2863	23 %
UL flame retardant rating	0.75mm	UL 94	HB
hardness	Test Condition	Test Method	ASAHI JAPAN/1300G
Rockwell hardness	M-Sale	ISO 2039-2	96
		R-Sale	ASTM D785	120
		M-Sale	ASTM D785	96
		R-Sale	ISO 2039-2	120
Basic Performance	Test Condition	Test Method	ASAHI JAPAN/1300G
Water absorption rate	湿		1.7 %
Other performance	Test Condition	Test Method	ASAHI JAPAN/1300G
Extreme Oxygen Index	干	ASTM D-2863	23 %
impact performance	Test Condition	Test Method	ASAHI JAPAN/1300G
Impact strength of simply supported beam without notch		ISO 179	72 kJ/m²

Supplier Join

Get App