'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA66 1300G ASAHI JAPAN
392
Form：Granules | Grade：Enhanced level
Properties:
High rigidityhigh strengthFatigue resistanceAnti creep
Typical Applications:
Electrical fieldElectronic fieldEngine hood partsAutomotive sectorcomponent
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Electrical field | Electronic field | Engine hood parts | Automotive sector | component |
| Properties: | High rigidity | high strength | Fatigue resistance | Anti creep |
Certificates
Technical Data Sheet
| other | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| characteristic | 高刚性 | |||
| Other performance | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | 干 | ASTM D-2863 | 23 | % |
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | ISO 179 | 72 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Extreme Oxygen Index | ASTM D2863 | 23 | % | |
| UL flame retardant rating | 0.75mm | UL 94 | HB | |
| Basic Performance | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | 湿 | 1.7 | % | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Elongation at Break | 干(湿) | ASTM D-638 | 3(5) | % |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(112) | R scale |
| Impact strength of cantilever beam gap | 干(湿) | ASTM D-256 | 127(147) | J/m |
| Taber abraser | 1000Cycles | ASTM D1044 | -- | mg |
| bending strength | 23°C | ISO 178 | 275 | Mpa |
| flexural coefficient | 干(湿) | ASTM D-790 | 9.3(6.3) | GPa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 96(75) | M Scale |
| bending strength | 干(湿) | ASTM D-790 | 289(216) | Mpa |
| tensile strength | 干(湿) | ASTM D-638 | 186(132) | Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 10000 | Mpa |
| tensile strength | ASTM D638 | 186 | Mpa | |
| Bending modulus | ASTM D790 | 9300 | Mpa | |
| 23°C | ISO 178 | 9000 | Mpa | |
| bending strength | ASTM D790 | 289 | Mpa | |
| tensile strength | Break,23°C | ISO 527-2 | 190 | Mpa |
| elongation | Break | ASTM D638 | 3.0 | % |
| Tensile strain | Break,23°C | ISO 527-2 | 3.0 | % |
| Bending modulus | ASTM D790/ISO 178 | 9320(MPa) | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 289(MPa) | kg·cm/cm(J/M)ft·lb/in | |
| Rockwell hardness | ASTM D785 | M96 | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| thermal conductivity | 0.30 | W/m/K | ||
| specific heat | 1590 | J/kg/°C | ||
| Linear coefficient of thermal expansion | MD | ASTM D696 | 3E-05 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 250 | °C |
| 1.8MPa,Unannealed | ASTM D648 | 250 | °C | |
| 0.45MPa,Unannealed | ISO 75-2/B | 265 | °C | |
| 0.45MPa,Unannealed | ASTM D648 | 260 | °C | |
| 0.46MPa,干 | ASTM D-648 | 260 | °C | |
| specific heat | 干 | 1590 | J/(kg.k) | |
| thermal conductivity | 干 | 0.3 | W/(m.K) | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 250 | °C |
| UL flame retardant rating | 干 | UL 94 | HB | |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 3 | ×10-5/K |
| Combustibility (rate) | UL 94 | HB | ||
| Hot deformation temperature | HDT | ASTM D648/ISO 75 | 250 | ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 3 | mm/mm.℃ | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | MD | Internal Method | 0.40 | % |
| TD | Internal Method | 0.90 | % | |
| 干 | 旭化成方法 | 0.4/0.9 | % | |
| Wear factor | 湿 | ASTM D-1044 | 15 | ×10-6kg/1000times |
| Shrinkage rate | 吸水率(Saturation,23°C) | Internal Method | -- | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO 62 | -- | % |
| density | ASTM D792/ISO 1183 | 1.39 | ||
| Shrinkage rate | ASTM D955 | 0.4-0.9 | % | |
| Water absorption rate | ASTM D570/ISO 62 | 1.7 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 | ohms·cm |
| ASTM D257 | 1E+15 | ohms·cm | ||
| Surface resistivity | IEC 60093 | 1E+15 | ohms | |
| ASTM D257 | 1E+15 | ohms | ||
| Dielectric strength | ASTM D149 | 28 | KV/mm | |
| Compared to the anti leakage trace index | 3.00mm | IEC 60112 | PLC 0 | |
| Dielectric strength | IEC 60243-1 | 28 | KV/mm | |
| Arc resistance | ASTM D495/IEC 60112 | 124 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Rockwell hardness | R-Sale | ISO 2039-2 | 120 | |
| M-Sale | ISO 2039-2 | 96 | ||
| R-Sale | ASTM D785 | 120 | ||
| M-Sale | ASTM D785 | 96 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.