PA6 TORAY JAPAN CM1017

Injection grade

US$ 3,530 / MT

FOB Guangzhou port, China

Physical properties	Test Condition	Test Method	TORAY JAPAN/CM1017
Water absorption rate	23°C,24hr	%	1.8 --
Shrinkage rate	MD：1.00mm3	%	0.50-1.0 --
density		ASTM D792/ISO 1183	1.13
Water absorption rate		ASTM D570/ISO 62	1.8 %
Taber abraser	1000g,CS-17	ASTM D-1044	3.5%水｜- mg/1000次
Shrinkage rate	MD：3.00mm4	%	1.0-1.6 --
Water absorption rate	Saturation,23°C	%	11 --
mechanical properties	Test Condition	Test Method	TORAY JAPAN/CM1017
Bending modulus	23°C	MPa	3000 1000
bending strength	-40℃	ASTM D-790	3.5%水｜1450 kg/cm2
Tensile strain	Break,23°C	%	38
Bending modulus	-40°C	MPa	3900 3600
shear strength	23°C	MPa	75.0 70.0
Impact strength of cantilever beam gap	Unnotched1/2"，23℃		3.5%水｜40 kg.cm/cm
tensile strength	23℃，Yield	ASTM D-638	3.5%水｜420 kg/cm2
Rockwell hardness		ASTM D785	83
Bending modulus	23℃	ASTM D-790	无水｜29000 kg/cm2
Bending modulus		80°C	MPa	800 400
Rockwell hardness	23℃	ASTM D-785	无水｜119 R-标度
compressive strength	23℃	ASTM D-695	无水｜890 kg/cm2
Impact strength of cantilever beam gap	23℃，Unnotched1/8		3.5%水｜- kg.cm/cm
Impact strength of cantilever beam gap		-40℃，Unnotched1/2		3.5%水｜15 kg.cm/cm
tensile strength	-40，Yield	ASTM D-638	3.5%水｜1150 kg/cm2
tensile strength		80°C	MPa	30.0 20.0
Friction coefficient vs. Metal			0.15to0.20 --
tensile strength	80℃，Yield	ASTM D-638	无水｜320 kg/cm2
bending strength	23°C	MPa	120 45.0
Bending modulus	80℃	ASTM D-790	无水｜8000 kg/cm2
bending strength	80°C	MPa	50.0 30.0
Compressive stress	23°C	MPa	85.0 --
bending strength	23℃	ASTM D-790	无水｜1100 kg/cm2
Bending modulus	-40℃	ASTM D-790	3.5%水｜37000 kg/cm2
tensile strength	-40°C	MPa	120 115
Elongation at Break	23℃	ASTM D-638	3.5%水｜<200 %
tensile strength	23°C	MPa	85.0 40.0
bending strength	80℃	ASTM D-790	3.5%水｜300 kg/cm2
Tensile strain	Yield,23°C	%	1.5 --
tensile strength	23℃，Break	ASTM D-638	3.5%水｜- kg/cm2
Shear strength	23℃	ASTM D-732	3.5%水｜690 kg/cm2
Taber abraser	1000Cycles	mg	3.00to4.00 --
bending strength	-40°C	MPa	145 140
Electrical performance	Test Condition	Test Method	TORAY JAPAN/CM1017
Dissipation factor	23°C,1MHz		0.030 0.13
Dielectric constant	23°C,1MHz		3.40 4.50
Arc resistance		sec	120 --
Volume resistivity		ASTM D-257	3.5%水｜1011-1012 Ω.cm
Dielectric strength		kV/mm	20 --
Dielectric constant	23°C,50Hz		4.10 9.00
Dissipation factor	23°C,1kHz		0.060 0.11
Dielectric constant	23°C,1kHz		3.90 8.00
Dissipation factor	106Hz	ASTM D-150	3.5%水｜-
Dissipation factor		23°C,50Hz		0.070 0.10
Dielectric constant	50HZ	ASTM D-150	3.5%水｜-
Arc resistance	1/8"	ASTM D-150	3.5%水｜-
Dielectric strength	1/8"	ASTM D-149	3.5%水｜- KV/mm
Dielectric constant	106Hz	ASTM D-150	3.5%水｜-
Volume resistivity		ASTM D257/IEC 60093	10^12-13 Ω.cm
Dissipation factor	103Hz	ASTM D-150	3.5%水｜-
Dissipation factor		50Hz	ASTM D-150	3.5%水｜-
Volume resistivity		ohms·cm	1.0E+14-1.0E+15 1.0E+11到1.0E+12
Compared to the Leakage Traceability Index (CTI)		UL 746	3.5%水｜- V
thermal performance	Test Condition	Test Method	TORAY JAPAN/CM1017
UL-94 flame retardant grade		UL 94	3.5%水｜-
specific heat		J/kg/°C	1900 --
Hot deformation temperature	HDT	ASTM D-648	无水｜190 °C
thermal conductivity			无水｜0.18 Kcal/m.hr.°C
Hot deformation temperature	HDT	ASTM D648/ISO 75	190 ℃（℉）
Melting temperature		°C	225 --
Hot deformation temperature	0.45MPa,Unannealed	°C	190 --
Hot deformation temperature		18.6kg/cm2	ASTM D-648	3.5%水｜- °C
specific heat			无水｜0.46 Cal/g.°C
Melting temperature		差示扫描测热计DSC法	225 °C
thermal conductivity		W/m/K	0.25 --
Linear coefficient of thermal expansion	MD	cm/cm/°C	8E-05 --
Linear coefficient of thermal expansion			ASTM D-696	无水｜8
Melting temperature			225 ℃（℉）
impact performance	Test Condition	Test Method	TORAY JAPAN/CM1017
Impact strength of simply supported beam without notch	-40°C		无断裂 --
Impact strength of simply supported beam without notch		23°C		无断裂 --
flammability	Test Condition	Test Method	TORAY JAPAN/CM1017
UL flame retardant rating	0.79mm		V-2 --
hardness	Test Condition	Test Method	TORAY JAPAN/CM1017
Rockwell hardness	R-Sale,23°C		119
Rockwell hardness		R-Sale,80°C		83 --
Basic Performance	Test Condition	Test Method	TORAY JAPAN/CM1017
Water absorption rate	23℃，24hr	ASTM D-570	3.5%水｜- %