Product Name / Manufacturer / Model

Grade

Reference Price

PPO SABIC INNOVATIVE SHANGHAI V0150B-701

Injection grade

US$ 3,950 / MT

FOB Shanghai port, China

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Shrinkage rate	--2，Flow	Internal Method	0.50 - 0.70 %
Melt Volume Flow Rate (MVR)	300°C/5.0 kg	ISO 1133	10.0 cm3/10min
Water absorption rate	Saturation, 23°C	ISO 62	0.18 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.060 %
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	3.5 g/10 min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.70 %
flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	775 °C
Extreme Oxygen Index		ISO 4589-2	32 %
Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	775 °C
Hot filament ignition temperature		1.0 mm	IEC 60695-2-13	775 °C
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960 °C
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating		2.0 mm	UL 94	5VA
injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Temperature at the front of the material cylinder			300 to 320 °C
Mold temperature			100 to 130 °C
Processing (melt) temperature			300 to 320 °C
Spray nozzle temperature			280 to 300 °C
drying temperature			110 to 120 °C
Temperature in the middle of the barrel			280 to 300 °C
drying time			2.0 to 3.0 hr
Hopper temperature			80 to 100 °C
Temperature at the rear of the barrel			260 to 280 °C
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Ae	130 °C
Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
Vicat softening temperature	--	ASTM D152511	155 °C
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span10	ISO 75-2/Be	140 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
Linear coefficient of thermal expansion		Flow : 23 to 80°C	ISO 11359-2	7.0E-5 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	145 °C
RTI Elec		UL 746	110 °C
RTI Imp		UL 746	105 °C
Vicat softening temperature	--	ISO 306/A50	160 °C
Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	9.0E-5 cm/cm/°C
Ball Pressure Test	140°C12	IEC 60695-10-2	通过
RTI		UL 746	115 °C
thermal conductivity		ISO 8302	0.27 W/m/K
Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	135 °C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	33 KV/mm
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Dielectric strength	3.20 mm, in Oil	IEC 60243-1	16 KV/mm
Relative permittivity	1 MHz	IEC 60250	2.70
Surface resistivity		IEC 60093	> 1.0E+15 ohms
Dielectric strength	1.60 mm, in Oil	IEC 60243-1	26 KV/mm
Dissipation factor	50 Hz	IEC 60250	9.0E-4
Relative permittivity	60 Hz	IEC 60250	2.80
Dissipation factor	60 Hz	IEC 60250	9.0E-4
Dissipation factor		1 MHz	IEC 60250	3.0E-3
Relative permittivity	50 Hz	IEC 60250	2.80
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Bending modulus	50.0 mm Span5	ASTM D790	2550 Mpa
bending strength	Yield, 50.0 mm Span5	ASTM D790	105 Mpa
elongation	Break	ISO 527-2/50	10 %
		Yield4	ASTM D638	5.0 %
		Yield	ISO 527-2/50	4.0 %
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	Internal Method	35.0 mg
elongation	Break4	ASTM D638	7.0 %
tensile strength	Break	ISO 527-2/50	55.0 Mpa
bending strength	--6,7	ISO 178	110 Mpa
tensile strength	Yield4	ASTM D638	70.0 Mpa
tensile strength		Yield	ISO 527-2/50	70.0 Mpa
Tensile modulus	--3	ASTM D638	2500 Mpa
Tensile modulus		--	ISO 527-2/1	2500 Mpa
Bending modulus	--6	ISO 178	2400 Mpa
tensile strength	Break4	ASTM D638	60.0 Mpa
impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0 kJ/m²
Dart impact	23°C, Total Energy	ASTM D3763	50.0 J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	14 kJ/m²
hardness	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/V0150B-701
Ball Pressure Test	H 358/30	ISO 2039-1	113 Mpa