PA66 A3X2G5 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 BASF GERMANY A3X2G5

Flame retardant grade

ULSGS

US$ 5,060 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	BASF GERMANY/A3X2G5
Volume resistivity	干/湿		10 Ω.cm
Surface resistivity		ASTM D257/IEC 60093	10^13/10^10 Ω
Dielectric strength	K20/P50，干/湿		80/65 KV/mm
Surface resistivity	干/湿		>10 Ω
Loss angle	1MHz，干/湿		0.02/0.1
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 525 M
Volume resistivity		ASTM D257/IEC 60093	10^15/10^12 Ω.cm
Dielectric constant	1MHz，干/湿		3.7/5
Physical properties	Test Condition	Test Method	BASF GERMANY/A3X2G5
Water absorption rate		ASTM D570/ISO 62	5.7-6.3 %
density		ASTM D792/ISO 1183	1.34
thermal performance	Test Condition	Test Method	BASF GERMANY/A3X2G5
Hot deformation temperature	HDT	ASTM D648/ISO 75	250 1.8Mpa ℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2.5-3.5/6-8 mm/mm.℃
Temperature index	在20000h/5000h，后拉伸强度下降50%时		139/157 °C
Maximum operating temperature			220 °C
Hot deformation temperature	0.45MPa负荷，Dry		250 °C
Hot deformation temperature		1.8MPa负荷，Dry		250 °C
specific heat	Dry		1.5 J/(g.K)
Linear coefficient of thermal expansion	（23-80）℃，Dry		2.5-3.5/6-8
thermal conductivity	Dry		0.27 W/(m.K)
Melting temperature			260 ℃（℉）
mechanical properties	Test Condition	Test Method	BASF GERMANY/A3X2G5
Impact strength of cantilever beam gap	+23℃，干/湿		11/17 KJ/m
elongation	≤0.5%, +23℃，湿		3500 Mpa
Charpy Notched Impact Strength	+23℃，干/湿		65/70 KJ/m
Charpy Notched Impact Strength			ASTM D256/ISO 179	13/17 kg·cm/cm(J/M)ft·lb/in
Elongation at Break	干/湿，V=50mm/min		3/4.5 %
Tensile modulus		ASTM D638/ISO 527	8500/6000 kg/cm²(MPa)[Lb/in²]
impact strength	+23℃，干/湿		4/10 J
Elongation at Break		ASTM D638/ISO 527	3/4.5 %
Fracture stress (V=50mm/min)	干/湿		140/100 Mpa
Charpy Notched Impact Strength	30℃，干		60 KJ/m
Tensile creep modulus	1000h,湿		3500 Mpa
Tensile modulus	干/湿		8500/6000 Mpa
Ball Pressure Test	干/湿		190 Mpa
tensile strength		ASTM D638/ISO 527	140/100 kg/cm²(MPa)[Lb/in²]
Bending modulus	干/湿		7100 Mpa
Tensile yield stress (V=50mm/min)	干/湿		140/100 Mpa
other	Test Condition	Test Method	BASF GERMANY/A3X2G5
characteristic			玻纤增强注射级.红磷阻燃剂长期稳定性.具有优异的机械性能和电性能