PA66 A3X2G5 BASF GERMANY

Form：Granules | Grade：Flame retardant grade

Properties:

Electrical performanceFlame retardantOil resistant

Typical Applications:

Electrical applicationsElectrical components

Supplier(1)

Product Description

Certificates(2)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Electrical components
Properties:	Electrical performance \| Flame retardant \| Oil resistant

Certificates

SGS

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			玻纤增强注射级.红磷阻燃剂长期稳定性.具有优异的机械性能和电性能
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Fracture stress (V=50mm/min)	干/湿		140/100	Mpa
tensile strength		ASTM D638/ISO 527	140/100	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	8500/6000	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	3/4.5	%
Charpy Notched Impact Strength		ASTM D256/ISO 179	-	kg·cm/cm(J/M)ft·lb/in
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256/ISO 179	13/17	kg·cm/cm(J/M)ft·lb/in
elongation	≤0.5%, +23℃，湿		3500	Mpa
Bending modulus	干/湿		7100	Mpa
Charpy Notched Impact Strength	30℃，干		60	KJ/m
Tensile yield stress (V=50mm/min)	干/湿		140/100	Mpa
Ball Pressure Test	干/湿		190	Mpa
Elongation at Break	干/湿，V=50mm/min		3/4.5	%
Charpy Notched Impact Strength	+23℃，干/湿		13/17	KJ/m
Impact strength of cantilever beam gap	+23℃，干/湿		11/17	KJ/m
Tensile modulus	干/湿		8500/6000	Mpa
Tensile creep modulus	1000h,湿		3500	Mpa
Elongation at Break	干/湿，V=50mm/min		3/4.5	%
impact strength	+23℃，干/湿		4/10	J
Charpy Notched Impact Strength	+23℃，干/湿		65/70	KJ/m
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Maximum operating temperature			220	°C
Linear coefficient of thermal expansion	（23-80）℃，Dry		2.5-3.5/6-8
Hot deformation temperature	0.45MPa负荷，Dry		250	°C
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	2.5-3.5/6-8	mm/mm.℃
Melting temperature			260	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	250 1.8Mpa	℃（℉）
thermal conductivity	Dry		0.27	W/(m.K)
Temperature index	在20000h/5000h，后拉伸强度下降50%时		139/157	°C
specific heat	Dry		1.5	J/(g.K)
Hot deformation temperature	1.8MPa负荷，Dry		250	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D570/ISO 62	5.7-6.3	%
density		ASTM D792/ISO 1183	1.34
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Loss angle	1MHz，干/湿		0.02/0.1
Surface resistivity	干/湿		>10	Ω
Volume resistivity	干/湿		10	Ω.cm
Dielectric strength	K20/P50，干/湿		80/65	KV/mm
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 500
Dielectric constant	1MHz，干/湿		3.7/5
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 525 M
Volume resistivity		ASTM D257/IEC 60093	10^15/10^12	Ω.cm
Surface resistivity		ASTM D257/IEC 60093	10^13/10^10	Ω

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.