PC DMX9455 BK1066 PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/DMX9455 BK1066
Water absorption rate	50% RH, equilib	ASTM D570	0.13 %
		50% RH, 24 hrs	ASTM D 570	0.04 %
		24 hours	ASTM D570	0.08 %
melt mass-flow rate	300℃/1.2 kg	ASTM D1238	14.5
Wear resistance		Internal	10
Water absorption rate	23°C / 50% RH	ISO 62	0.13 %
Water absorption rate		equilibrium, 23C	ASTM D570	0.28 %
Wear resistance		ASTM D 1044	10
Vertical (Flow)	3.2 mm	Internal	0.5-0.8 %
Water absorption rate	23°C/sat	ISO 62	0.27 %
Bi Rong		ASTM D792	0.85
Melt Volume Flow Rate (MVR)		ISO 1133	13
impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/DMX9455 BK1066
Suspended wall beam without notch impact strength	23℃	ASTM D4812	NB J/m
Impact strength of cantilever beam gap	80103，23℃	ISO 180/1A	5 kJ/m²
Suspended wall beam without notch impact strength	80103，23℃	ISO 180/1U	NB kJ/m²
Impact strength of cantilever beam gap	23℃	ASTM D256	30 J/m
Charpy Notched Impact Strength	V-notch Edgew 80103 sp=62mm，23℃	ISO 179/1eA	3 kJ/m²
Impact strength of cantilever beam gap	80103，30℃	ISO 180/1A	4 kJ/m²
Total energy at 23 ℃ (73 ℉)		ASTM D3763	30
Charpy Notched Impact Strength	V-notch Edgew 80103 sp=62mm，-30℃	ISO 179/1eA	3 kJ/m²
Impact strength of cantilever beam gap	30℃	ASTM D256	30 J/m
mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/DMX9455 BK1066
Bending modulus	1.3 mm/min, 50 mm span	ASTM D790	2600 Mpa
Tensile modulus	1 mm/min	ISO 527	2450 Mpa
Yield (yld)	Type I, 50 mm/min，Yield	ASTM D638	7 Mpa
Fracture (brk)	50 mm/min	ISO 527	40 Mpa
Tensile modulus	50 mm/min	ASTM D638	2900 Mpa
Yield (yld)	1.3 mm/min, 50 mm span，Yield	ASTM D790	120 Mpa
Bending modulus	2 mm/min	ISO 178	2450 Mpa
Yield (yld)	50 mm/min，Yield	ISO 527	7 Mpa
Yield (yld)		2 mm/min，Yield	ISO 178	108 Mpa
Fracture (brk)	Type I, 50 mm/min	ASTM D638	70 Mpa