PC DMX9455 BK1066 SABIC INNOVATIVE NANSHA

Form：Granules | Grade：Transparent level

Properties:

scratch resistance copolymerwear resistantFlame retardanttransparent

Typical Applications:

Bottle capFitness equipmentAutomotive sectorElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Bottle cap \| Fitness equipment \| Automotive sector \| Electronic field \| Electrical field
Properties:	scratch resistance \| copolymer \| wear resistant \| Flame retardant \| transparent

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	V-notch Edgew 80103 sp=62mm，-30℃	ISO 179/1eA	3	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	V-notch Edgew 80103 sp=62mm，23℃	ISO 179/1eA	3	kJ/m²
Impact strength of cantilever beam gap	30℃	ASTM D256	30	J/m
	Impact strength of cantilever beam gap	80103，30℃	ISO 180/1A	4	kJ/m²
		Impact strength of cantilever beam gap	23℃	ASTM D256	30	J/m
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	80103，23℃	ISO 180/1A	5	kJ/m²
Suspended wall beam without notch impact strength	23℃	ASTM D4812	NB	J/m
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	80103，23℃	ISO 180/1U	NB	kJ/m²
Total energy at 23 ℃ (73 ℉)		ASTM D3763	30
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Yield (yld)	Type I, 50 mm/min，Yield	ASTM D638	80	Mpa
Yield (yld)	Yield (yld)	50 mm/min，Yield	ISO 527	80	Mpa
Fracture (brk)	50 mm/min	ISO 527	60	Mpa
Fracture (brk)	Fracture (brk)	Type I, 50 mm/min	ASTM D638	65	Mpa
Yield (yld)	Type I, 50 mm/min，Yield	ASTM D638	7	%
Yield (yld)	Yield (yld)	50 mm/min，Yield	ISO 527	7	%
Fracture (brk)	Type I, 50 mm/min	ASTM D638	70	%
Fracture (brk)	Fracture (brk)	50 mm/min	ISO 527	40	%
Yield (yld)	1.3 mm/min, 50 mm span，Yield	ASTM D790	120	Mpa
Yield (yld)	Yield (yld)	2 mm/min，Yield	ISO 178	108	Mpa
Bending modulus	1.3 mm/min, 50 mm span	ASTM D790	2600	Mpa
Bending modulus	Bending modulus	2 mm/min	ISO 178	2450	Mpa
Tensile modulus	50 mm/min	ASTM D638	2900	Mpa
Tensile modulus	Tensile modulus	1 mm/min	ISO 527	2450	Mpa
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)		ISO 1133	13
melt mass-flow rate	300℃/1.2 kg	ASTM D1238	14.5
Vertical (Flow)	3.2 mm	Internal	0.5-0.8	%
Water absorption rate	24 hours	ASTM D570	0.08	%
	Water absorption rate	50% RH, equilib	ASTM D570	0.13	%
		Water absorption rate	equilibrium, 23C	ASTM D570	0.28	%
			Water absorption rate	23°C/sat	ISO 62	0.27	%
				Water absorption rate	23°C / 50% RH	ISO 62	0.13	%
				Water absorption rate	Water absorption rate	50% RH, 24 hrs	ASTM D 570	0.04	%
Bi Rong		ASTM D792	0.85
Wear resistance		Internal	10
Wear resistance	Wear resistance		ASTM D 1044	10

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.