PPS A400M D1 PPS vs. - Plastic Material Properties Comparison Chart at Plas.com

Electrical performance	Test Condition	Test Method	TORAY JAPAN/A400M D1
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
Dielectric strength		ASTM D-149	15 MV/m
Induced positive connection	10	ASTM D-150	0.002
Arc resistance	W电极	ASTM D-495	128 秒
Dielectric constant	10	ASTM D-150	5.0
Dielectric constant		23°C,1MHz	IEC 60250	4.90
Volume resistivity		IEC 60093	1E+16 ohms·cm
Dielectric strength		IEC 60243-1	22 KV/mm
Inherent resistance of volume		ASTM D-257	10 Ω.m
mechanical properties	Test Condition	Test Method	TORAY JAPAN/A400M D1
tensile strength	Yield,23°C	ISO 527-2	170 Mpa
limiting pv value		东丽法	815 KJ/m
Impact strength of cantilever beam gap	Notched23℃	ASTM D-256	100 J/m
abrasion		ASTM D-1044	70 mg/1000回
bending strength	23°C	ISO 178	255 Mpa
Elongation at Break		ASTM D-732	65
Friction coefficient	对钢	ASTM D-1894	0.28
bending strength		ASTM D-790	15.1 Mpa
Bending modulus	23°C	ISO 178	18500 Mpa
Shore hardness		ASTM D-785	122 洛氏
Impact strength of cantilever beam gap	Unnotched23℃	ASTM D-256	25 KJ/m
Tensile strain	Break,23°C	ISO 527-2	1.3 %
tensile strength		ASTM D-638	1.3 Mpa
Physical properties	Test Condition	Test Method	TORAY JAPAN/A400M D1
Water absorption rate	23°C,24hr	ISO 62	0.020 %
	320℃,98MPa,1mm厚，Flow长	东丽法	110
Shrinkage rate	垂重方向	东丽法	0.55 %
		TD:3.00mm2	Internal Method	0.75 %
		MD:3.00mm4	Internal Method	0.16 %
		Flow	东丽法	0.15 %
thermal performance	Test Condition	Test Method	TORAY JAPAN/A400M D1
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.8E-05 cm/cm/°C
Melting temperature		DSC	278 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	3E-05 cm/cm/°C
Hot deformation temperature	1.82MPa	ASTM D-648	>260 °C
Linear coefficient of thermal expansion	Flow	ASTM D-696	1.7
Linear coefficient of thermal expansion		垂重方向	ASTM D-696	2.5
Combustibility		UL -94	V-0
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260 °C
Melting temperature		ISO 11357-3	278 °C
Basic Performance	Test Condition	Test Method	TORAY JAPAN/A400M D1
Water absorption rate		ASTM D-570	0.02 %
impact performance	Test Condition	Test Method	TORAY JAPAN/A400M D1
Impact strength of simply supported beam without notch	23°C	ISO 179	30 kJ/m²
Supplementary Information	Test Condition	Test Method	TORAY JAPAN/A400M D1
BarFlowLength	320°C,1.00mm	Internal Method	115 mm
flammability	Test Condition	Test Method	TORAY JAPAN/A400M D1
UL flame retardant rating	0.36mm	UL 94	V-0
hardness	Test Condition	Test Method	TORAY JAPAN/A400M D1
Rockwell hardness	R-Scale	ISO 2039-2	122