PPS A400M D1 TORAY JAPAN

Form：Granules

Properties:

Glass fiber reinforcedFlame retardantFiller: Glass mineral55% filler by weight

Typical Applications:

Electrical applications

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications
Properties:	Glass fiber reinforced \| Flame retardant \| Filler: Glass mineral \| 55% filler by weight

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	30	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.36mm	UL 94	V-0
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D-570	0.02	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Shore hardness		ASTM D-785	122	洛氏
Impact strength of cantilever beam gap	Unnotched23℃	ASTM D-256	25	KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Notched23℃	ASTM D-256	100	J/m
Elongation at Break		ASTM D-732	65
bending strength		ASTM D-790	15.1	GPa
abrasion		ASTM D-1044	70	mg/1000回
Friction coefficient	对钢	ASTM D-1894	0.28
tensile strength		ASTM D-638	1.3	%
limiting pv value		东丽法	815	KJ/m
tensile strength		ASTM D-638	145	Mpa
bending strength		ASTM D-790	190	Mpa
tensile strength	Yield,23°C	ISO 527-2	170	Mpa
Tensile strain	Break,23°C	ISO 527-2	1.3	%
Bending modulus	23°C	ISO 178	18500	Mpa
bending strength	23°C	ISO 178	255	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.82MPa	ASTM D-648	>260	°C
Melting temperature		DSC	278	°C
Linear coefficient of thermal expansion	垂重方向	ASTM D-696	2.5
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ASTM D-696	1.7
Combustibility		UL -94	V-0
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	260	°C
Melting temperature		ISO 11357-3	278	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	3E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	垂重方向	东丽法	0.55	%
Shrinkage rate	Shrinkage rate	Flow	东丽法	0.15	%
	320℃,98MPa,1mm厚，Flow长	东丽法	110
Shrinkage rate	TD:3.00mm2	Internal Method	0.75	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	Internal Method	0.16	%
Water absorption rate	23°C,24hr	ISO 62	0.020	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength		ASTM D-149	15	MV/m
Dielectric constant	10	ASTM D-150	5.0
Induced positive connection	10	ASTM D-150	0.002
Arc resistance	W电极	ASTM D-495	128	秒
Inherent resistance of volume		ASTM D-257	10	Ω.m
Volume resistivity		IEC 60093	1E+16	ohms·cm
Dielectric strength		IEC 60243-1	22	KV/mm
Dielectric constant	23°C,1MHz	IEC 60250	4.90
Dissipation factor	23°C,1MHz	IEC 60250	2E-03
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	122
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
BarFlowLength	320°C,1.00mm	Internal Method	115	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.