PA66 A4H PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 BASF GERMANY A4H

Injection grade

US$ 6,960 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	BASF GERMANY/A4H
Volume resistivity	干/湿		10 Ω.cm
Dielectric strength	K20/P50，干/湿		110/80 KV/mm
Loss angle	1MHz，干/湿		0.025/0.2
Surface resistivity	干/湿		10 Ω
Compared to the Leakage Traceability Index (CTI)	干/湿		CTI 575 M
Dielectric strength	23℃	V/mil	840
Dielectric constant	1MHz，干/湿		3.2/5
Volume resistivity	23℃	ohms·cm	1.0E+12-1.0E+14
Physical properties	Test Condition	Test Method	BASF GERMANY/A4H
Shrinkage rate	23℃	%	0.10-0.31
Saturation, 23 ℃		%	3.5to5.0
Balance, 23 ℃, 50% RH		%	1.2to1.5
hardness	Test Condition	Test Method	BASF GERMANY/A4H
Ball Pressure Test			222.76to370.34 MPa
thermal performance	Test Condition	Test Method	BASF GERMANY/A4H
Hot deformation temperature	HDT	ASTM D648/ISO 75	220 ℃（℉）
Melting temperature		°C	260
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	7-10 mm/mm.℃
1.8MPa, unannealed		°C	230to250
Temperature index	在20000h/5000h，后拉伸强度下降50%时		118/138 °C
Maximum operating temperature			>200 °C
Hot deformation temperature	0.45MPa负荷，Dry		220 °C
Hot deformation temperature		1.8MPa负荷，Dry		75 °C
specific heat	Dry		1.7 J/(g.K)
8.0Mpa, unannealed		°C	65to220
Linear coefficient of thermal expansion	（23-80）℃，Dry		7-10
flow		mm/mm/°C	142.2E-5-203.2E-5
transverse		mm/mm/°C	68.6E-5-127.0E-5
thermal conductivity	Dry		0.23 W/(m.K)
Continuous use temperature		°C	110to220
mechanical properties	Test Condition	Test Method	BASF GERMANY/A4H
Impact strength of cantilever beam gap	+23℃，干/湿		5.5/NB KJ/m
elongation	≤0.5%, +23℃，湿		700 Mpa
Charpy Notched Impact Strength	+23℃，干/湿		NB/NB KJ/m
elongation		ASTM D638/ISO 527	4.2/20 %
Charpy Notched Impact Strength	+23℃，干/湿字段1_文本		8/30 KJ/m
impact strength	-20℃,干		20 J
tensile strength	Break,23℃		144.83to292.41 MPa
Elongation at Break	干/湿，V=50mm/min		4.2/20 %
Tensile modulus	23℃		8206.9to28000.0 MPa
Tensile strain	Break,23℃	%	1.9to3.1
impact strength	+23℃，干/湿		50/>140 J
Elongation at Break		ASTM D638/ISO 527	4.2/20 %
Fracture stress (V=50mm/min)	干/湿		85/50 Mpa
Tensile creep modulus	1000h,湿		700 Mpa
Tensile modulus	干/湿		3100/1200 Mpa
Ball Pressure Test	干/湿		160/100 Mpa
Impact strength of cantilever beam gap	-30℃,干		7 KJ/m
Bending modulus		ASTM D790/ISO 178	3000 kg·cm/cm(J/M)ft·lb/in
Bending modulus		干/湿		3000 Mpa
Tensile yield stress (V=50mm/min)	干/湿		85/50 Mpa
impact performance	Test Condition	Test Method	BASF GERMANY/A4H
Impact strength of simply supported beam without notch	23℃	kJ/m²	11.143to19.964