PA6 BKV25F30 PA6 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA6 LANXESS GERMANY BKV25F30

Injection grade

US$ 3,170 / MT

FOB Guangzhou port, China

flammability	Test Condition	Test Method	LANXESS GERMANY/BKV25F30
Hot filament ignition temperature	0.8mm	IEC 60695-2-13	775 °C
Burning wire flammability index	1.5mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	0.40mm	IEC 60695-2-13	850 °C
Burning wire flammability index	0.40mm	IEC 60695-2-12	960 °C
UL flame retardant rating	3.0mm	UL 94	V-0
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850 °C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	0.40mm	UL 94	V-0
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	775 °C
UL flame retardant rating	1.0mm	UL 94	V-0
Burning wire flammability index	0.8mm	IEC 60695-2-12	960 °C
BurningBehavior		ISO 3795	passed
mechanical properties	Test Condition	Test Method	LANXESS GERMANY/BKV25F30
Tensile strain	Break,23°C	ISO 527-2/5	2.3 %
Bending strain	23°C	ISO 178/A	2.5 %
Bending modulus	23°C	ISO 178/A	10000 Mpa
bending strength	23°C	ISO 178/A	230 Mpa
tensile strength	Break,23°C	ISO 527-2/5	150 Mpa
Tensile modulus	23°C	ISO 527-2/1	11000 Mpa
Physical properties	Test Condition	Test Method	LANXESS GERMANY/BKV25F30
Shrinkage rate	TD:120°C,4hr,2.00mm3	ISO 2577	0.10 %
		MD:280°C,2.00mm2	ISO 2577	0.30 %
		TD:280°C,2.00mm2	ISO 2577	0.60 %
		MD:120°C,4hr,2.00mm3	ISO 2577	0.10 %
thermal performance	Test Condition	Test Method	LANXESS GERMANY/BKV25F30
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	9E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215 °C
Vicat softening temperature		ISO 306/B120	205 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	222 °C
impact performance	Test Condition	Test Method	LANXESS GERMANY/BKV25F30
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	3.00 J
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	1000 N
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	55 kJ/m²
Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	900 N
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	45 kJ/m²
Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	1.90 J
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	45 kJ/m²
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	50 kJ/m²
Electrical performance	Test Condition	Test Method	LANXESS GERMANY/BKV25F30
Volume resistivity	23°C	IEC 60093	3.4E+14 ohms·cm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Surface resistivity		IEC 60093	4.1E+13 ohms
Supplementary Information	Test Condition	Test Method	LANXESS GERMANY/BKV25F30
ISO Shortcut		ISO 1874	PA6.GFHR.14-110.GF25