'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA6 BKV25F30 LANXESS GERMANY
137
Form：Granules | Grade：Injection grade
Properties:
Heat aging
Typical Applications:
Automotive componentsInstrument componentsElectronic and Electrical ApplicationsIndustrial applicationsCommunication equipment
Product Description
Certificates(1)
Datasheet
Product Description
| Typical Applications: | Automotive components | Instrument components | Electronic and Electrical Applications | Industrial applications | Communication equipment |
| Properties: | Heat aging |
Certificates
Technical Data Sheet
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Multi axis Instrumented Peak Impact Force | 23°C | ISO 6603-2 | 1000 | N |
| -30°C | ISO 6603-2 | 900 | N | |
| Multi axis Instrumented Impact Energy | 23°C | ISO 6603-2 | 3.00 | J |
| -30°C | ISO 6603-2 | 1.90 | J | |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 50 | kJ/m² |
| -30°C | ISO 180/1U | 45 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 45 | kJ/m² |
| 23°C | ISO 179/1eU | 55 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| UL flame retardant rating | 0.40mm | UL 94 | V-0 | |
| 1.0mm | UL 94 | V-0 | ||
| BurningBehavior | ISO 3795 | passed | ||
| Hot filament ignition temperature | 3.0mm | IEC 60695-2-13 | 850 | °C |
| 1.5mm | IEC 60695-2-13 | 775 | °C | |
| 0.8mm | IEC 60695-2-13 | 775 | °C | |
| 0.40mm | IEC 60695-2-13 | 850 | °C | |
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 | °C |
| 1.5mm | IEC 60695-2-12 | 960 | °C | |
| 0.8mm | IEC 60695-2-12 | 960 | °C | |
| 0.40mm | IEC 60695-2-12 | 960 | °C | |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | 23°C | ISO 527-2/1 | 11000 | Mpa |
| bending strength | 23°C | ISO 178/A | 230 | Mpa |
| Bending strain | 23°C | ISO 178/A | 2.5 | % |
| tensile strength | Break,23°C | ISO 527-2/5 | 150 | Mpa |
| Tensile strain | Break,23°C | ISO 527-2/5 | 2.3 | % |
| Bending modulus | 23°C | ISO 178/A | 10000 | Mpa |
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO 11359-2 | 2E-05 | cm/cm/°C |
| Melting temperature | ISO 11357-3 | 222 | °C | |
| Vicat softening temperature | ISO 306/B120 | 205 | °C | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO 75-2/A | 205 | °C |
| 0.45MPa,Unannealed | ISO 75-2/B | 215 | °C | |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 9E-05 | cm/cm/°C |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Shrinkage rate | TD:280°C,2.00mm2 | ISO 2577 | 0.60 | % |
| TD:120°C,4hr,2.00mm3 | ISO 2577 | 0.10 | % | |
| MD:280°C,2.00mm2 | ISO 2577 | 0.30 | % | |
| MD:120°C,4hr,2.00mm3 | ISO 2577 | 0.10 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Compared to the anti leakage trace index | SolutionA | IEC 60112 | PLC 1 | |
| Volume resistivity | 23°C | IEC 60093 | 3.4E+14 | ohms·cm |
| Surface resistivity | IEC 60093 | 4.1E+13 | ohms | |
| Supplementary Information | Test Condition | Test Method | Test Result | Test Unit |
| ISO Shortcut | ISO 1874 | PA6.GFHR.14-110.GF25 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.