Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PC TEIJIN SINGAPORE LV-2225Z

High liquidity level

US$ 3,460 / MT

FOB Dongguan Port

mechanical properties	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
bending strength		ISO 178	94.0 Mpa
Tensile modulus		ISO 527-2/1	2400 Mpa
Nominal tensile fracture strain		ISO 527-2/50	>50 %
bending strength		ASTM D790/ISO 178	94 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	2130 kg/cm²(MPa)[Lb/in²]
tensile strength	Yield	ISO 527-2/50	61.0 Mpa
Elongation at Break		ASTM D638/ISO 527	50 %
Rockwell hardness		ASTM D785	M 77
Bending modulus		ISO 178	2400 Mpa
Tensile strain	Yield	ISO 527-2/50	6.0 %
Bending modulus		ASTM D790/ISO 178	2260 kg/cm²(MPa)[Lb/in²]
flammability	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
Burning wire flammability index	1.5mm	IEC 60695-2-12	850 °C
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875 °C
UL flame retardant rating	3.0mm	UL 94	V-2
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	0.40mm	UL 94	V-2
UL flame retardant rating		1.5mm	UL 94	V-2
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	850 °C
Physical properties	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70 %
Water absorption rate	23°C,24hr	ISO 62	0.20 %
Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	15.0 cm3/10min
density		ASTM D792/ISO 1183	1.2
optical performance	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
Transmittance rate		ASTM D1003/ISO 13468	88 %
Refractive index		ASTM D542/ISO 489	1.585
transmissivity	3000μm	ASTM D1003	88.0 %
Refractive index		ASTM D542	1.585
Electrical performance	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
Dielectric constant	100Hz	IEC 60250	3.10
Dissipation factor	100Hz	IEC 60250	1E-03
Compared to the anti leakage trace index		IEC 60112	PLC 3
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	9E-03
Surface resistivity		IEC 60093	>1.0E+15 ohms
Dielectric strength		IEC 60243-1	30 KV/mm
Dielectric constant	1MHz	IEC 60250	3.00
other	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
characteristic			低粘度抗紫外线性能良好
purpose			电子电器领域应用透明或半透明配件电器用具
thermal performance	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
RTI Str	1.5mm	UL 746	125 °C
RTI Imp	1.5mm	UL 746	115 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	141 °C
Vicat softening temperature		ASTM D1525/ISO R306	148 ℃（℉）
Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	125 °C
Combustibility (rate)		UL 94	V-2
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
Vicat softening temperature		ISO 306/B50	146 °C
impact performance	Test Condition	Test Method	TEIJIN SINGAPORE/LV-2225Z
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak