PC LV-2225Z TEIJIN SINGAPORE

Form：Granules | Grade：High liquidity level

Properties:

Low viscositytransparentUV resistance

Typical Applications:

Electrical fieldElectronic fieldcurrency

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| currency
Properties:	Low viscosity \| transparent \| UV resistance

Certificates

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ASTM D542	1.585
transmissivity	3000μm	ASTM D1003	88.0	%
Transmittance rate		ASTM D1003/ISO 13468	88	%
Refractive index		ASTM D542/ISO 489	1.585
other	Test Condition	Test Method	Test Result	Test Unit
characteristic			低粘度抗紫外线性能良好
purpose			电子电器领域应用透明或半透明配件电器用具
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	NoBreak
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40mm	UL 94	V-2
	UL flame retardant rating	1.5mm	UL 94	V-2
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	V-2
Burning wire flammability index	1.5mm	IEC 60695-2-12	850	°C
Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.5mm	IEC 60695-2-13	850	°C
Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875	°C
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Nominal tensile fracture strain		ISO 527-2/50	>50	%
Bending modulus		ISO 178	2400	Mpa
bending strength		ISO 178	94.0	Mpa
Tensile modulus		ISO 527-2/1	2400	Mpa
tensile strength	Yield	ISO 527-2/50	61.0	Mpa
Tensile strain	Yield	ISO 527-2/50	6.0	%
Elongation at Break		ASTM D638/ISO 527	50	%
Tensile modulus		ASTM D638/ISO 527	2130	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M 77
Bending modulus		ASTM D790/ISO 178	2260	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	94	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	141	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Vicat softening temperature		ISO 306/B50	146	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05	cm/cm/°C
RTI Elec	1.5mm	UL 746	125	°C
RTI Imp	1.5mm	UL 746	115	°C
RTI Str	1.5mm	UL 746	125	°C
Combustibility (rate)		UL 94	V-2
Vicat softening temperature		ASTM D1525/ISO R306	148	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	15.0	cm3/10min
Shrinkage rate	TD:4.00mm	Internal Method	0.50-0.70	%
Shrinkage rate	Shrinkage rate	MD:4.00mm	Internal Method	0.50-0.70	%
Water absorption rate	23°C,24hr	ISO 62	0.20	%
density		ASTM D792/ISO 1183	1.2
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength		IEC 60243-1	30	KV/mm
Dielectric constant	100Hz	IEC 60250	3.10
Dielectric constant	Dielectric constant	1MHz	IEC 60250	3.00
Dissipation factor	100Hz	IEC 60250	1E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	9E-03
Compared to the anti leakage trace index		IEC 60112	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.