PC/PBT
PC/PBT SABIC INNOVATIVE US 6370-8A6D030
Injection grade
US$ 3,060 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
bending strengthISO 178154 Mpa
Tensile strainBreakISO 527-2/5110 %
BreakASTM D6384.0 %
Tensile modulusASTM D6389750 Mpa
bending strengthBreak,50.0mmSpanASTM D790138 Mpa
Yield,50.0mmSpanASTM D790150 Mpa
tensile strengthBreakASTM D63891.0 Mpa
YieldISO 527-2/5105 Mpa
Bending modulusISO 1787750 Mpa
Tensile strainYieldISO 527-2/53.0 %
Bending modulus50.0mmSpanASTM D7905380 Mpa
Tensile modulusISO 527-2/18500 Mpa
tensile strengthBreakISO 527-2/53.00 Mpa
Tensile strainYieldASTM D6383.0 %
tensile strengthYieldASTM D63897.0 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Shrinkage rateTD：--3Internal Method0.70-0.90 %
TD：--2Internal Method0.40-0.70 %
Water absorption rate24hrASTM D5700.090 %
melt mass-flow rate250°C/5.0kgASTM D123824 g/10min
Specific volumeASTM D7920.700 cm³/g
Melt Volume Flow Rate (MVR)265°C/5.0kgISO 113319.0 cm3/10min
250°C/5.0kgISO 113312.0 cm3/10min
Shrinkage rateMD：--3Internal Method0.40-0.50 %
MD：--2Internal Method0.30-0.40 %
Water absorption rateEquilibrium,23°C,50%RHISO 620.15 %
Saturation,23°CISO 620.50 %
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Dielectric strength1.60mm,in OilASTM D14927 KV/mm
Hot wire ignitionHWIUL 746PLC 1
Compared to the anti leakage trace indexCTIUL 746PLC 2
High arc combustion indexHAIUL 746PLC 3
Dielectric constant100HzASTM D1504.00
High voltage arc tracing rateHVTRUL 746PLC 1
Dissipation factor1MHzASTM D1500.020
Volume resistivityASTM D2574.8E+15 ohms·cm
Arc resistanceASTM D495PLC 5
Dielectric strength3.20mm,inAirASTM D14920 KV/mm
Dissipation factor100HzASTM D1503E-03
Dielectric constant1MHzASTM D1504.00
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Linear coefficient of thermal expansionTD：-40to40°CASTME8311.1E-04 cm/cm/°C
RTI StrUL 746140 °C
Linear coefficient of thermal expansionTD：-40to40°CISO 11359-21.1E-04 cm/cm/°C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af155 °C
Vicat softening temperature--ISO 306/B50148 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648163 °C
1.8MPa,Unannealed,6.40mmASTM D648149 °C
Linear coefficient of thermal expansionMD：60to138°CASTME8312E-05 cm/cm/°C
MD：-40to40°CISO 11359-22.7E-05 cm/cm/°C
Hot deformation temperature0.45MPa,Unannealed,6.40mmASTM D648204 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8312.7E-05 cm/cm/°C
RTI ElecUL 746140 °C
RTI ImpUL 746130 °C
Vicat softening temperature--ISO 306/B120150 °C
ASTM D152512153 °C
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
UL flame retardant rating1.5mmUL 94HB
hardnessTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Rockwell hardnessR-ScaleASTM D785109
impact performanceTest ConditionTest MethodSABIC INNOVATIVE US/6370-8A6D030
Impact strength of cantilever beam gap23°CISO 180/1A10 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA9.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D376317.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
Dart impact23°C,EnergyatPeakLoadASTM D37635.00 J

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China