POM TR-20 POM vs. - Plastic Material Properties Comparison Chart at Plas.com

Electrical performance	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
Dielectric strength	3.00mm	IEC 60243-1	21 KV/mm
Volume resistivity		IEC 60093	2E+14 ohms·cm
Surface resistivity		IEC 60093	9E+15 ohms
mechanical properties	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
bending strength		ISO 178	96.0 Mpa
Wear factor	0.060MPa,0.15m/sec5	JISK7218	500 10^-8mm³/N·m
Friction coefficient	Dynamic2	JISK7218	0.34
Wear factor	0.060MPa,0.15m/sec6	JISK7218	7000 10^-8mm³/N·m
Tensile strain	Break	ISO 527-2	5.0 %
Friction coefficient	Steel - Dynamic3	JISK7218	0.56
Tensile modulus		ISO 527-2	4500 Mpa
Wear factor	0.49MPa,0.30m/sec4	JISK7218	150 10^-8mm³/N·m
Wear factor		0.49MPa,0.30m/sec7	JISK7218	8000 10^-8mm³/N·m
Bending modulus		ISO 178	4100 Mpa
tensile strength		ISO 527-2	59.0 Mpa
impact performance	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.0 kJ/m²
Physical properties	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
Water absorption rate	23°C,24hr	ISO 62	0.50 %
density		ISO 1183	1.53 g/cm³
melt mass-flow rate	190°C/2.16kg	ISO 1133	21 g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	16.0 cm3/10min
flammability	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
UL flame retardant rating		UL 94	HB
Supplementary Information	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
ColourNumber			CF2001/CD3501
thermal performance	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	8E-05 cm/cm/°C
Linear coefficient of thermal expansion		MD：23to55°C	Internal Method	8E-05 cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125 °C
hardness	Test Condition	Test Method	TAIWAN POLYPLASTICS/TR-20
Rockwell hardness	M-Scale	ISO 2039-2	75