POM TR-20 TAIWAN POLYPLASTICS

Form：Granules | Grade：Fill level

Properties:

enhanceHigh rigidity

Typical Applications:

Automotive sectorIndustrial machineryElectronic fieldElectrical field

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive sector \| Industrial machinery \| Electronic field \| Electrical field
Properties:	enhance \| High rigidity

Certificates

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Friction coefficient	Steel - Dynamic3	JISK7218	0.56
Tensile strain	Break	ISO 527-2	5.0	%
tensile strength		ISO 527-2	59.0	Mpa
Tensile modulus		ISO 527-2	4500	Mpa
Wear factor	0.49MPa,0.30m/sec7	JISK7218	8000	10^-8mm³/N·m
	Wear factor	0.060MPa,0.15m/sec6	JISK7218	7000	10^-8mm³/N·m
		Wear factor	0.060MPa,0.15m/sec5	JISK7218	500	10^-8mm³/N·m
		Wear factor	Wear factor	0.49MPa,0.30m/sec4	JISK7218	150	10^-8mm³/N·m
Friction coefficient	Dynamic2	JISK7218	0.34
bending strength		ISO 178	96.0	Mpa
Bending modulus		ISO 178	4100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD：23to55°C	Internal Method	8E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	Internal Method	8E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	125	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.50	%
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	16.0	cm3/10min
melt mass-flow rate	190°C/2.16kg	ISO 1133	21	g/10min
density		ISO 1183	1.53	g/cm³
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric strength	3.00mm	IEC 60243-1	21	KV/mm
Volume resistivity		IEC 60093	2E+14	ohms·cm
Surface resistivity		IEC 60093	9E+15	ohms
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	75
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			CF2001/CD3501

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.