PA66 70G25HSLR NC010 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA66 DUPONT SHENZHEN 70G25HSLR NC010

Enhanced level

US$ 4,050 / MT

FOB Shenzhen Port

Physical properties	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.4 %
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate		横向Flow	ISO 294-4	1.1 %
Flow Length	2.00 mm		350 mm
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0 %
Stickiness		ISO 307	150 cm³/g
flammability	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
雾化 - G-value (condensate)		ISO 6452	5.0E-4 g
FMVSS combustion rate		FMVSS 302	B
Burning rate	1.00 mm	ISO 3795	26 mm/min
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
bending strength		ISO 178	260 Mpa
Tensile strain	Break	ISO 527-2	3.0 %
tensile strength	Break	ISO 527-2	180 Mpa
Tensile modulus		ISO 527-2	8500 Mpa
Bending modulus		ISO 178	8000 Mpa
thermal performance	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	261 °C
Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.1E-4 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	252 °C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	3.3E-5 cm/cm/°C
Glass transition temperature		ISO 11357-2	80.0 °C
Melting temperature		ISO 11357-3	262 °C
Vicat softening temperature		ISO 306/B50	257 °C
injection	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
Melt Temperature, Optimum			295 °C
Hold Pressure Time			3.00 s/mm
Mold temperature			70 to 120 °C
Processing (melt) temperature			285 to 305 °C
drying temperature			80 °C
Maximum Screw Tangential Speed			12 m/min
Mold Temperature, Optimum			100 °C
Maintain pressure			50.0 to 100 Mpa
Maintain pressure		Drying Recommended		yes
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.20 %
Filling analysis	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
Melt density			1.15 g/cm³
Odor		VDA 270	3.50
Thermal Conductivity of Melt			0.21 W/m/K
Top out temperature			210 °C
Specific Heat Capacity of Melt			2090 J/kg/°C
Electrical performance	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
Dissipation factor	100 Hz	IEC 62631-2-1	7.0E-3
Compared to the anti leakage trace index		IEC 60112	PLC 1
Relative permittivity	100 Hz	IEC 62631-2-1	3.60
Volume resistivity		IEC 62631-3-1	1.0E+13 ohms·m
Surface resistivity		IEC 62631-3-2	-- ohms
impact performance	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	60 kJ/m²
hardness	Test Condition	Test Method	DUPONT SHENZHEN/70G25HSLR NC010
Ball Pressure Test	H 961/30	ISO 2039-1	260 Mpa