'%20/%3e%3cg%20opacity='1'%20transform='translate(150.5%200)%20rotate(0)'%3e%3cpath%20id='路径%204'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M494%20472.601L487%20410.101L460%20472.601L494%20472.601Z'%3e%3c/path%3e%3cpath%20id='路径%203'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M80%20620.761C152%20676.261%20250%20670.761%20264.5%20670.761C351%20664.261%20412.5%20636.261%20443.5%20620.761C536%20572.261%20580.45%20516.261%20599.5%20492.261C566.05%20492.261%20483.5%20492.261%20465.5%20492.261C408%20532.761%20385.5%20541.761%20369%20550.261C262.5%20599.761%20214%20591.261%20184%20591.261C81%20584.761%2024.3%20510.211%200%20478.261C23%20580.261%2067.5%20609.261%2080%20620.761Z'%3e%3c/path%3e%3cpath%20id='路径%202'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M427.998%202.26C325.498%2014.26%20222.068%2073.64%20247.998%2063.76C384.498%2011.76%20427.998%2024.76%20437.998%2024.76C526.998%2041.76%20559.998%2085.76%20568.998%2095.76C606.498%20142.26%20611.398%20187.06%20613.498%20206.26C631.458%20206.26%20679.498%20206.26%20703.998%20206.26C692.998%20109.26%20633.378%2063.91%20622.998%2056.26C563.998%2012.76%20513.248%205.41%20491.498%202.26C467.498%20-2.24%20437.168%201.19%20427.998%202.26Z'%3e%3c/path%3e%3cpath%20id='路径%201'%20fill-rule='evenodd'%20style='fill:%23C70000'%20opacity='1'%20d='M232%20206.763C243%20178.763%20262%20156.763%20273.5%20140.263C329%2080.2634%20374%2069.7634%20410.5%2061.2634C446.5%2052.2634%20499%2061.2634%20504.5%2061.2634C446%2039.7634%20393%2040.7634%20387.5%2040.7634C308.5%2047.2634%20259.5%2075.2634%20237%2088.7634C162.5%20135.263%20122.95%20185.313%20106%20206.763C139.86%20206.763%20221.5%20206.763%20232%20206.763Z'%3e%3c/path%3e%3c/g%3e%3cpath%20id='减去顶层'%20fill-rule='evenodd'%20style='fill:%23003686'%20opacity='1'%20d='M379.519,227.698l4.237,4.101l-38.576,198.188h98.804l3.966,3.839l-7.614,38.817h-147.091l-4.064,-3.934l46.975,-241.011zM900.883,363.706c-21,-8.75%20-34.89067,-17.22667%20-41.672,-25.43c-6.78133,-8.20333%20-10.172,-19.19533%20-10.172,-32.976c0,-24.06267%208.832,-43.75033%2026.496,-59.063c17.664,-15.312%2040.55067,-22.968%2068.66,-22.968c11.266,0%2022.231,1.121%2032.895,3.363c10.664,2.242%2020.974,5.60533%2030.93,10.09l-8.139,40.672l-5.05,2.827c-6.54467,-5.18467%20-13.96233,-9.21167%20-22.253,-12.081c-9.95333,-3.44533%20-21.00033,-5.168%20-33.141,-5.168c-12.906,0%20-23.406,3.08967%20-31.5,9.269c-8.09333,6.18%20-12.14,14.08233%20-12.14,23.707c0,9.18733%2010.06233,18.32%2030.187,27.398l1.149,0.493l19.031,8.367c15.96867,7.10933%2027.64433,15.668%2035.027,25.676c7.38267,10.00733%2011.074,22.28467%2011.074,36.832c0,25.156%20-8.80467,45.226%20-26.414,60.21c-17.60933,14.98467%20-41.39833,22.477%20-71.367,22.477c-12.03133,0%20-24.30867,-1.422%20-36.832,-4.266c-12.52333,-2.84333%20-25.56633,-7.16367%20-39.129,-12.961l8.62,-44.559l4.63,-2.592c9.52333,7.45333%2019.435,13.24467%2029.735,17.374c11.59333,4.64867%2023.24167,6.973%2034.945,6.973c14.54667,0%2025.97633,-3.19933%2034.289,-9.598c8.31267,-6.39867%2012.469,-15.06667%2012.469,-26.004c0,-6.78133%20-1.914,-12.66%20-5.742,-17.636c-3.82867,-4.97667%20-9.51633,-9.051%20-17.063,-12.223zM54.3672,227.698h68.9058c25.81267,0%2045.473,5.004%2058.981,15.012c13.50733,10.008%2020.261,24.58233%2020.261,43.723c0,12.46867%20-1.996,24.82767%20-5.988,37.077c-3.992,12.25%20-9.16,21.98467%20-15.504,29.204c-8.53133,9.95267%20-19.14067,17.14433%20-31.828,21.575c-12.68733,4.42867%20-29.14817,6.643%20-49.3825,6.643h-26.9063l-17.8828,91.711h-43.7778l-3.88732,-3.761zM642.062,227.698h59.063l18.238,240.969l-4.109,3.976h-43.66l-2.297,-60.539h-0.041l-1.756,-40.844l-0.04,-0.002l-3.249,-98.607l-41.151,94.615l-0.06,-0.006l-20.5,47.5h0.005l-25.411,57.883h-43.849l-3.589,-3.474zM94.7266,268.386l-13.7813,71.859h23.4607c15.96867,0%2027.918,-3.69133%2035.848,-11.074c7.92933,-7.38267%2011.894,-18.457%2011.894,-33.223c0,-9.95333%20-2.84367,-17.03533%20-8.531,-21.246c-5.68733,-4.21067%20-15.367,-6.316%20-29.039,-6.316z'%3e%3c/path%3e%3c/svg%3e)
PA66 70G25HSLR NC010 DUPONT SHENZHEN
145
Form：Granules | Grade：Enhanced level
Properties:
High rigidityHigh temperature resistan
Typical Applications:
Bottle capAutomotive ApplicationsElectrical applications
Product Description
Certificates(0)
Datasheet
Product Description
| Typical Applications: | Bottle cap | Automotive Applications | Electrical applications |
| Properties: | High rigidity | High temperature resistan |
Certificates
No Data...
Technical Data Sheet
| Filling analysis | Test Condition | Test Method | Test Result | Test Unit |
|---|---|---|---|---|
| Melt density | 1.15 | g/cm³ | ||
| Top out temperature | 210 | °C | ||
| Specific Heat Capacity of Melt | 2090 | J/kg/°C | ||
| Thermal Conductivity of Melt | 0.21 | W/m/K | ||
| Odor | VDA 270 | 3.50 | ||
| impact performance | Test Condition | Test Method | Test Result | Test Unit |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 60 | kJ/m² |
| 23°C | ISO 179/1eU | 60 | kJ/m² | |
| flammability | Test Condition | Test Method | Test Result | Test Unit |
| Burning rate | 1.00 mm | ISO 3795 | 26 | mm/min |
| UL flame retardant rating | UL 94 | HB | ||
| UL 94 | HB | |||
| FMVSS combustion rate | FMVSS 302 | B | ||
| 雾化 - G-value (condensate) | ISO 6452 | 5.0E-4 | g | |
| mechanical properties | Test Condition | Test Method | Test Result | Test Unit |
| Tensile modulus | ISO 527-2 | 8500 | Mpa | |
| tensile strength | Break | ISO 527-2 | 180 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.0 | % |
| Bending modulus | ISO 178 | 8000 | Mpa | |
| bending strength | ISO 178 | 260 | Mpa | |
| injection | Test Condition | Test Method | Test Result | Test Unit |
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 to 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 285 to 305 | °C | ||
| Melt Temperature, Optimum | 295 | °C | ||
| Mold temperature | 70 to 120 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| Maintain pressure | 50.0 to 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min | ||
| thermal performance | Test Condition | Test Method | Test Result | Test Unit |
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 261 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 252 | °C | |
| Glass transition temperature | ISO 11357-2 | 80.0 | °C | |
| Vicat softening temperature | ISO 306/B50 | 257 | °C | |
| Melting temperature | ISO 11357-3 | 262 | °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 3.3E-5 | cm/cm/°C |
| Across Flow | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Physical properties | Test Condition | Test Method | Test Result | Test Unit |
| Water absorption rate | Saturation, 23°C, 2.00 mm | ISO 62 | 6.4 | % |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % | |
| Stickiness | ISO 307 | 150 | cm³/g | |
| Flow Length | 2.00 mm | 350 | mm | |
| Shrinkage rate | Flow | ISO 294-4 | 0.30 | % |
| 横向Flow | ISO 294-4 | 1.1 | % | |
| Electrical performance | Test Condition | Test Method | Test Result | Test Unit |
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume resistivity | IEC 62631-3-1 | 1.0E+13 | ohms·m | |
| Relative permittivity | 100 Hz | IEC 62631-2-1 | 3.60 | |
| Dissipation factor | 100 Hz | IEC 62631-2-1 | 7.0E-3 | |
| Compared to the anti leakage trace index | IEC 60112 | PLC 1 | ||
| hardness | Test Condition | Test Method | Test Result | Test Unit |
| Ball Pressure Test | H 961/30 | ISO 2039-1 | 260 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.