LCP DUPONT USA 6130L-WT010

Injection grade

US$ 8,790 / MT

FOB Guangzhou port, China

Physical properties	Test Condition	Test Method	DUPONT USA/6130L-WT010
Water absorption rate		ASTM D570/ISO 62	0.002 %
density		ASTM D792/ISO 1183	1680
thermal performance	Test Condition	Test Method	DUPONT USA/6130L-WT010
Hot deformation temperature	HDT	ASTM D648/ISO 75	268 ℃（℉）
Linear coefficient of thermal expansion	MD	ISO 11359-2	3E-06 cm/cm/°C
Linear coefficient of thermal expansion		TD	ISO 11359-2	7E-05 cm/cm/°C
Melting temperature			335 ℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	265 °C
Melting temperature		ISO 11357-3	335 °C
other	Test Condition	Test Method	DUPONT USA/6130L-WT010
characteristic			30%玻纤增强
Electrical performance	Test Condition	Test Method	DUPONT USA/6130L-WT010
Surface resistivity		ASTM D257/IEC 60093	1.00E+16 Ω
Dissipation factor	2.05GHz	Internal Method	5E-03
Compared to the anti leakage trace index		IEC 60112	PLC 3
Volume resistivity		IEC 60093	>1.0E+16 ohms·cm
Volume resistivity			ASTM D257/IEC 60093	1.00E+17 Ω.cm
Dissipation factor	1MHz	IEC 60250	0.031
Surface resistivity		IEC 60093	>1.0E+16 ohms
Relative permittivity	1MHz	IEC 60250	4.00
Dielectric strength		IEC 60243-1	36 KV/mm
Relative permittivity	2.05GHz	Internal Method	4.16
mechanical properties	Test Condition	Test Method	DUPONT USA/6130L-WT010
Tensile strain	Break	ISO 527-2/1A/5	1.8 %
bending strength		ASTM D790/ISO 178	195 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ISO 527-2/1A/1	13000 Mpa
Tensile modulus			ASTM D638/ISO 527	13500 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2.7 %
tensile strength	Break	ISO 527-2/1A/5	130 Mpa
Bending modulus	23°C	ISO 178	12000 Mpa
Impact strength of cantilever beam gap		ASTM D256/ISO 179	25 kg·cm/cm(J/M)ft·lb/in
tensile strength		ASTM D638/ISO 527	165 kg/cm²(MPa)[Lb/in²]
impact performance	Test Condition	Test Method	DUPONT USA/6130L-WT010
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35 kJ/m²
flammability	Test Condition	Test Method	DUPONT USA/6130L-WT010
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating		0.38mm	UL 94	V-0