LCP 6130L-WT010 DUPONT USA

127

Form：Granules | Grade：Injection grade

Properties:

Glass fiber reinforcedFiller: Glass fiber reinf30%Filler by weight

Typical Applications:

Household appliancesAutomotive sectorAerospaceElectronic fieldElectrical fieldAerospace ApplicationsCommunication equipmentApplication in the automotive field

Supplier(4)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Household appliances \| Automotive sector \| Aerospace \| Electronic field \| Electrical field \| Aerospace Applications \| Communication equipment \| Application in the automotive field
Properties:	Glass fiber reinforced \| Filler: Glass fiber reinf \| 30% \| Filler by weight

Certificates

No Data...

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			30%玻纤增强
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	0.38mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23°C	ISO 178	12000	Mpa
Tensile strain	Break	ISO 527-2/1A/5	1.8	%
tensile strength	Break	ISO 527-2/1A/5	130	Mpa
bending strength		ASTM D790/ISO 178	195	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	165	kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	13500	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	2.7	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	20	kg·cm/cm(J/M)ft·lb/in
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256/ISO 179	25	kg·cm/cm(J/M)ft·lb/in
Tensile modulus		ISO 527-2/1A/1	13000	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	3E-06	cm/cm/°C
Melting temperature		ISO 11357-3	335	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	265	°C
Melting temperature			335	℃（℉）
Hot deformation temperature	HDT	ASTM D648/ISO 75	268	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate		ASTM D570/ISO 62	0.002	%
density		ASTM D792/ISO 1183	1680
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm
Surface resistivity		IEC 60093	>1.0E+16	ohms
Volume resistivity		ASTM D257/IEC 60093	1.00E+17	Ω.cm
Surface resistivity		ASTM D257/IEC 60093	1.00E+16	Ω
Dielectric strength		IEC 60243-1	36	KV/mm
Relative permittivity	1MHz	IEC 60250	4.00
Relative permittivity	Relative permittivity	2.05GHz	Internal Method	4.16
Dissipation factor	1MHz	IEC 60250	0.031
Dissipation factor	Dissipation factor	2.05GHz	Internal Method	5E-03
Compared to the anti leakage trace index		IEC 60112	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

LCP 6130L-WT010 DUPONT USA

Product Description

Certificates

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index