ASA
ASA SABIC INNOVATIVE SHANGHAI CR7500 BK1041
Impact resistant grade
US$ 2,550 / MT
FOB Shanghai port, China
injectionTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Back pressure0.300 to 1.00 Mpa
Temperature at the front of the material cylinder245 to 260 °C
Spray nozzle temperature235 to 255 °C
Screw speed30 to 80 rpm
Mold temperature60 to 85 °C
Exhaust hole depth0.038 to 0.076 mm
Processing (melt) temperature255 to 270 °C
drying temperature85 to 95 °C
Suggested injection volume40 to 80 %
Temperature in the middle of the barrel235 to 255 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.040 %
Temperature at the rear of the barrel230 to 250 °C
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CR7500 BK1041
bending strength--5,6ISO 17864.0 Mpa
elongationYield3ASTM D6383.6 %
BreakISO 527-2/519 %
Bending modulus50.0 mm Span4ASTM D7902170 Mpa
elongationBreak3ASTM D63860 %
bending strengthYield, 50.0 mm Span4ASTM D79068.0 Mpa
tensile strengthBreakISO 527-2/535.0 Mpa
Yield3ASTM D63840.0 Mpa
elongationYieldISO 527-2/53.3 %
Tensile modulus--2ASTM D6381970 Mpa
--ISO 527-2/12040 Mpa
tensile strengthYieldISO 527-2/543.0 Mpa
Bending modulus--5ISO 1782060 Mpa
tensile strengthBreak3ASTM D63833.0 Mpa
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Vicat softening temperature--ISO 306/B50102 °C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8319.5E-5 cm/cm/°C
Across Flow : -40°CISO 11359-29.5E-5 cm/cm/°C
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D64890.0 °C
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span9ISO 75-2/Ae88.0 °C
Ball Pressure Test98°CIEC 60695-10-2通过
Vicat softening temperature--ISO 306/B120105 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8ISO 75-2/Af89.0 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8318.4E-5 cm/cm/°C
Vicat softening temperature--ASTM D15251098.0 °C
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Melt Volume Flow Rate (MVR)220°C/10.0 kgISO 11336.00 cm3/10min
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.20 %
Saturation, 23°CISO 620.50 %
melt mass-flow rate220°C/10.0 kgASTM D12386.3 g/10 min
Melt Volume Flow Rate (MVR)260°C/5.0 kgISO 113310.0 cm3/10min
melt mass-flow rate260°C/5.0 kgASTM D123811 g/10 min
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.80 %
impact performanceTest ConditionTest MethodSABIC INNOVATIVE SHANGHAI/CR7500 BK1041
Dart impact23°C, Total EnergyASTM D376330.0 J

Supplier Join

Contact Us

Get App

Top

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index

+86 0755 27873515

Room 906, Global Digital Building, No. 9 Gaoxin Middle 3rd Road, Maling Community, Yuehai Subdistrict, Nanshan District, Shenzhen, Guangdong Province, China