PPS JAPAN POLYPLASTIC 6565A6

Injection grade

US$ 5,870 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
bending strength		ISO 178	165 Mpa
Tensile strain	Break	ISO 527-2	1.0 %
bending strength		ASTM D790/ISO 178	165 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	1 %
Impact strength of cantilever beam gap		ASTM D256/ISO 179	4.5 kg·cm/cm(J/M)ft·lb/in
Bending modulus		ISO 178	18200 Mpa
tensile strength		ISO 527-2	125 Mpa
tensile strength			ASTM D638/ISO 527	125 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	18200 kg/cm²(MPa)[Lb/in²]
Electrical performance	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
Dielectric strength	3.00mm	IEC 60243-1	16 KV/mm
Dissipation factor	1kHz	IEC 60250	0.013
Dissipation factor		耐电弧性	IEC 60250	189 sec
Relative permittivity	1kHz	IEC 60250	5.40
Compared to the anti leakage trace index		IEC 60112	PLC 3
Volume resistivity		IEC 60093	2E+16 ohms·cm
Volume resistivity			ASTM D257/IEC 60093	2.0 x 10^ 16 Ω.cm
Dissipation factor	1MHz	IEC 60250	5E-03
Relative permittivity	1MHz	IEC 60250	5.40
Physical properties	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
Water absorption rate		ASTM D570/ISO 62	0.01 %
Water absorption rate		23°C,24hr	ISO 62	0.010 %
Melt viscosity	310°C,1000sec^-1	ISO 11443	280000 mPa·s
density		ASTM D792/ISO 1183	1.96
Supplementary Information	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
ColourNumber			HF2000/HD9050
other	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
characteristic			低温模具.良好树脂间粘接性
thermal performance	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
Linear coefficient of thermal expansion	MD	Internal Method	1E-05 cm/cm/°C
Vicat softening temperature		ASTM D1525/ISO R306	275 ℃（℉）
Combustibility (rate)		UL 94	V-0
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	275 °C
Linear coefficient of thermal expansion	TD	Internal Method	3E-05 cm/cm/°C
flammability	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
UL flame retardant rating		UL 94	V-0
hardness	Test Condition	Test Method	JAPAN POLYPLASTIC/6565A6
Rockwell hardness	M-Scale	ISO 2039-2	95