PPS 6565A6 JAPAN POLYPLASTIC

164

Form：Granules | Grade：Injection grade

Properties:

transparentHigh temperature resistanHigh mobilityFlame retardantGlass fiber reinforced

Typical Applications:

Electronic fieldElectrical field

Supplier(2)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Electronic field \| Electrical field
Properties:	transparent \| High temperature resistan \| High mobility \| Flame retardant \| Glass fiber reinforced

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			低温模具.良好树脂间粘接性
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ASTM D790/ISO 178	18200	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	165	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	125	kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	1	%
Impact strength of cantilever beam gap		ASTM D256/ISO 179	4.5	kg·cm/cm(J/M)ft·lb/in
bending strength		ISO 178	165	Mpa
Bending modulus		ISO 178	18200	Mpa
Tensile strain	Break	ISO 527-2	1.0	%
tensile strength		ISO 527-2	125	Mpa
Elongation at Break		ASTM D638/ISO 527	1	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TD	Internal Method	3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	Internal Method	1E-05	cm/cm/°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	275	°C
Combustibility (rate)		UL 94	V-0
Vicat softening temperature		ASTM D1525/ISO R306	275	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.010	%
Melt viscosity	310°C,1000sec^-1	ISO 11443	280000	mPa·s
density		ASTM D792/ISO 1183	1.96
Water absorption rate		ASTM D570/ISO 62	0.01	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D257/IEC 60093	2.0 x 10^ 16	Ω.cm
Relative permittivity	1MHz	IEC 60250	5.40
Relative permittivity	Relative permittivity	1kHz	IEC 60250	5.40
Dielectric strength	3.00mm	IEC 60243-1	16	KV/mm
Volume resistivity		IEC 60093	2E+16	ohms·cm
Compared to the anti leakage trace index		IEC 60112	PLC 3
Dissipation factor	耐电弧性	IEC 60250	189	sec
	Dissipation factor	1MHz	IEC 60250	5E-03
	Dissipation factor	Dissipation factor	1kHz	IEC 60250	0.013
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Scale	ISO 2039-2	95
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ColourNumber			HF2000/HD9050

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top