PBT 5101G-30U PBT vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PBT TORAY JAPAN 5101G-30U

Enhanced level

US$ 2,880 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	TORAY JAPAN/5101G-30U
Dissipation factor	23°C,1MHz	IEC 60250	0.020
Dielectric constant	50Hz	ASTM D150	3.9
Dissipation factor	23°C,50Hz	IEC 60250	2E-03
Volume resistivity		IEC 60093	1E+17 ohms·cm
Volume resistivity			ASTM D257	5.0
Arc resistance		ASTM D495	130 S
Dielectric constant	23°C,1kHz	IEC 60250	3.70
Dielectric constant		23°C,50Hz	IEC 60250	3.90
Dielectric loss	50Hz，Tangent	ASTM D150	0.002
Arc resistance		IEC 60950	130 sec
Dielectric loss	10，Tangent	ASTM D150	0.02
Dielectric constant	10	ASTM D150	3.7
Dielectric strength		ASTM D149	31 MV/m
mechanical properties	Test Condition	Test Method	TORAY JAPAN/5101G-30U
Bending modulus	23℃	ASTM D790	7.0 GPa
tensile strength	23°C	ISO 527-2	130 Mpa
bending strength	23°C	ISO 178	205 Mpa
Friction coefficient	对金属	ASTM D1894	0.15
bending strength	23℃	ASTM D790	185 Mpa
elongation	23℃	ASTM D638	5 %
Friction coefficient	对本身	ASTM D1894	0.19
Bending modulus	23°C	ISO 178	8000 Mpa
Friction coefficient vs. Metal		SuzukiMethod	0.15
Friction coefficient			0.19
Rockwell hardness		ASTM D785	89 M
Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D256	85 KJ/m
Tensile modulus	23°C	ISO 527-2	8500 Mpa
Impact strength of cantilever beam gap	Notched，23℃	ASTM D256	145 J/m
Tensile strain	Break,23°C	ISO 527-2	4.0 %
tensile strength	23℃	ASTM D638	130 Mpa
Physical properties	Test Condition	Test Method	TORAY JAPAN/5101G-30U
Water absorption rate	23°C,24hr	ISO 62	0.070 %
Shrinkage rate	MD:3.00mm3	Internal Method	0.40 %
Water absorption rate	23℃,24hr	ASTM D570	0.07 %
Shrinkage rate	TD:3.00mm2	Internal Method	1.0 %
thermal performance	Test Condition	Test Method	TORAY JAPAN/5101G-30U
Linear coefficient of thermal expansion		ASTM D696	2.5
Hot deformation temperature	0.45MPa	ASTM D648	225 °C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO 11359-2	4.2E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220 °C
UL flame retardant rating		UL 94	HB
Hot deformation temperature	1.82Mpa	ASTM D648	215 °C
Hot deformation temperature		1.8MPa,Unannealed	ISO 75-2/A	205 °C
hardness	Test Condition	Test Method	TORAY JAPAN/5101G-30U
Rockwell hardness	M-Sale,23°C	ISO 2039-2	60
flammability	Test Condition	Test Method	TORAY JAPAN/5101G-30U
UL flame retardant rating		UL 94	HB
Supplementary Information	Test Condition	Test Method	TORAY JAPAN/5101G-30U
BarFlowLength	250°C,1.00mm	Internal Method	6.70 CM
impact performance	Test Condition	Test Method	TORAY JAPAN/5101G-30U
Impact strength of simply supported beam without notch	23°C	ISO 179	65 kJ/m²