PBT 5101G-30U TORAY JAPAN

106

Form：Granules | Grade：Enhanced level

Properties:

High impact resistanceFast forming cycle

Typical Applications:

Automotive ApplicationsElectrical components

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electrical components
Properties:	High impact resistance \| Fast forming cycle

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23°C	ISO 179	65	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	23°C	ISO 527-2	8500	Mpa
tensile strength	23°C	ISO 527-2	130	Mpa
Friction coefficient	对本身	ASTM D1894	0.19
Friction coefficient	Friction coefficient	对金属	ASTM D1894	0.15
Rockwell hardness		ASTM D785	89	M
Impact strength of cantilever beam gap	Unnotched，23℃	ASTM D256	85	KJ/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	Notched，23℃	ASTM D256	145	J/m
Bending modulus	23℃	ASTM D790	7.0	GPa
bending strength	23℃	ASTM D790	185	Mpa
elongation	23℃	ASTM D638	5	%
tensile strength	23℃	ASTM D638	130	Mpa
Tensile strain	Break,23°C	ISO 527-2	4.0	%
Bending modulus	23°C	ISO 178	8000	Mpa
bending strength	23°C	ISO 178	205	Mpa
Friction coefficient			0.19
Friction coefficient vs. Metal		SuzukiMethod	0.15
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating		UL 94	HB
Linear coefficient of thermal expansion		ASTM D696	2.5
Hot deformation temperature	1.82Mpa	ASTM D648	215	°C
	Hot deformation temperature	0.45MPa	ASTM D648	225	°C
		Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	220	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	205	°C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO 11359-2	4.2E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23°C,24hr	ISO 62	0.070	%
Shrinkage rate	MD:3.00mm3	Internal Method	0.40	%
Shrinkage rate	Shrinkage rate	TD:3.00mm2	Internal Method	1.0	%
Water absorption rate	23℃,24hr	ASTM D570	0.07	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	10	ASTM D150	3.7
Dielectric constant	Dielectric constant	50Hz	ASTM D150	3.9
Dielectric strength		ASTM D149	31	MV/m
Volume resistivity		ASTM D257	5.0
Arc resistance		ASTM D495	130	S
Dielectric loss	10，Tangent	ASTM D150	0.02
Dielectric loss	Dielectric loss	50Hz，Tangent	ASTM D150	0.002
Volume resistivity		IEC 60093	1E+17	ohms·cm
Dielectric constant	23°C,50Hz	IEC 60250	3.90
Dielectric constant	Dielectric constant	23°C,1kHz	IEC 60250	3.70
Dissipation factor	23°C,50Hz	IEC 60250	2E-03
Dissipation factor	Dissipation factor	23°C,1MHz	IEC 60250	0.020
Arc resistance		IEC 60950	130	sec
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	M-Sale,23°C	ISO 2039-2	60
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
BarFlowLength	250°C,1.00mm	Internal Method	6.70	CM

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top