PA66 A RV 300 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PA66 RADIC ITALY A RV 300

Injection grade

US$ 3,760 / MT

FOB Shenzhen Port

Physical properties	Test Condition	Test Method	RADIC ITALY/A RV 300
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	7.0 %
density		ISO 1183	1.35 g/cm³
Shrinkage rate	Flow	ISO 294-4	0.30 %
Shrinkage rate		横向Flow	ISO 294-4	1.0 %
Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.7 %
mechanical properties	Test Condition	Test Method	RADIC ITALY/A RV 300
bending strength		ISO 178	275 Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.9 %
Tensile modulus		ISO 527-2/1A/1	9500 Mpa
tensile strength	Break	ISO 527-2/1A/5	180 Mpa
Bending modulus		ISO 178	8500 Mpa
injection	Test Condition	Test Method	RADIC ITALY/A RV 300
Dew Point - Hot Air Drying Machine			-20 °C
Injection speed			中等偏快
Drying temperature - hot air dryer			80 °C
Mold temperature			80 to 100 °C
Processing (melt) temperature			280 to 300 °C
Drying time - hot air dryer			2.0 to 4.0 hr
Suggested maximum moisture content			0.15 %
impact performance	Test Condition	Test Method	RADIC ITALY/A RV 300
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	75 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13 kJ/m²
flammability	Test Condition	Test Method	RADIC ITALY/A RV 300
flammability		FMVSS 302	0 mm/min
Burning wire flammability index	2.0 mm	IEC 60695-2-12	700 °C
UL flame retardant rating	0.8 mm	UL 94	HB
Electrical performance	Test Condition	Test Method	RADIC ITALY/A RV 300
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 0
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
Surface resistivity		IEC 60093	1.0E+12 ohms
thermal performance	Test Condition	Test Method	RADIC ITALY/A RV 300
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	250 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/Af	235 °C
Melting temperature		ISO 11357-3	260 °C
Vicat softening temperature		ISO 306/B50	245 °C