PA66 A RV 300 RADIC ITALY

Form：Granules | Grade：Injection grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	75	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8 mm	UL 94	HB
Burning wire flammability index	2.0 mm	IEC 60695-2-12	700	°C
flammability		FMVSS 302	0	mm/min
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2/1A/1	9500	Mpa
tensile strength	Break	ISO 527-2/1A/5	180	Mpa
Tensile strain	Break	ISO 527-2/1A/5	3.9	%
Bending modulus		ISO 178	8500	Mpa
bending strength		ISO 178	275	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Drying temperature - hot air dryer			80	°C
Drying time - hot air dryer			2.0 to 4.0	hr
Dew Point - Hot Air Drying Machine			-20	°C
Suggested maximum moisture content			0.15	%
Processing (melt) temperature			280 to 300	°C
Mold temperature			80 to 100	°C
Injection speed			中等偏快
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/Bf	250	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/Af	235	°C
Vicat softening temperature		ISO 306/B50	245	°C
Melting temperature		ISO 11357-3	260	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.35	g/cm³
Shrinkage rate	横向Flow	ISO 294-4	1.0	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.30	%
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	7.0	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	1.7	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1.0E+12	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Compared to the anti leakage trace index	Solution A	IEC 60112	PLC 0

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.