PA6 LANXESS GERMANY BKV330 H2.0

Flame retardant grade

US$ 2,990 / MT

FOB Guangzhou port, China

film	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Thin film puncture strength	--7	ISO 6603-2	883 J
Thin film puncture strength		--6	ISO 6603-2	791 J
thermal performance	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Vicat softening temperature	--	ISO 306/B50	>200 °C
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1E-04 cm/cm/°C
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	90.0 °C
Hot deformation temperature		0.45MPa,Unannealed	ISO 75-2/B	215 °C
Vicat softening temperature	--	ISO 306/B120	>200 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200 °C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05 cm/cm/°C
Melting temperature		ISO 11357-3	222 °C
mechanical properties	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Tensile strain	Break,23°C	ISO 527-2/5	3.0 %
Bending modulus	23°C	ISO 178/A	8300 Mpa
bending strength	23°C	ISO 178	260 Mpa
tensile strength	Break,23°C	ISO 527-2/5	170 Mpa
Tensile modulus	23°C	ISO 527-2/1	9800 Mpa
bending strength	FlexuralStrainatFlexuralStrength5(23°C)		4.5 %
bending strength		3.5%Strain	ISO 178/A	245 Mpa
Physical properties	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.060 %
		TD:280°C,2.00mm2	ISO 294-4	0.70 %
		TD:120°C,2hr,2.00mm3	ISO 294-4	0.070 %
		MD:280°C,2.00mm2	ISO 294-4	0.35 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.3 %
Water absorption rate		Saturation,23°C	ISO 62	6.5 %
Apparent density		ISO 60	0.70 g/cm³
hardness	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Ball Pressure Test		ISO 2039-1	195 Mpa
Electrical performance	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Volume resistivity	23°C	IEC 60093	1E+15 ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	32 KV/mm
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
Surface resistivity		IEC 60093	1E+13 ohms
Relative permittivity	23°C,100Hz	IEC 60250	4.50
Dissipation factor	23°C,100Hz	IEC 60250	0.019
Relative permittivity	23°C,1MHz	IEC 60250	3.90
flammability	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Extreme Oxygen Index		ISO 4589-2	23 %
UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	700 °C
UL flame retardant rating	1.6mm	UL 94	HB
BurningBehavior		ISO 3795	passed
impact performance	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	65 kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	75 kJ/m²
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	75 kJ/m²
Supplementary Information	Test Condition	Test Method	LANXESS GERMANY/BKV330 H2.0
ISO Shortcut		ISO 1874	PA6.GHR.14-100.GF30