PA6 BKV330 H2.0 LANXESS GERMANY

Form：Granules | Grade：Flame retardant grade

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	75	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	75	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.6mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	HB
Burning wire flammability index	2.0mm	IEC 60695-2-12	700	°C
Extreme Oxygen Index		ISO 4589-2	23	%
BurningBehavior		ISO 3795	passed
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile strain	Break,23°C	ISO 527-2/5	3.0	%
Bending modulus	23°C	ISO 178/A	8300	Mpa
bending strength	3.5%Strain	ISO 178/A	245	Mpa
	bending strength	23°C	ISO 178	260	Mpa
	bending strength	bending strength	FlexuralStrainatFlexuralStrength5(23°C)		4.5	%
Tensile modulus	23°C	ISO 527-2/1	9800	Mpa
tensile strength	Break,23°C	ISO 527-2/5	170	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	8.0MPa,Unannealed	ISO 75-2/C	90.0	°C
Vicat softening temperature	--	ISO 306/B50	>200	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	>200	°C
Melting temperature		ISO 11357-3	222	°C
Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	1E-04	cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	215	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	200	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Apparent density		ISO 60	0.70	g/cm³
Shrinkage rate	TD:280°C,2.00mm2	ISO 294-4	0.70	%
	Shrinkage rate	TD:120°C,2hr,2.00mm3	ISO 294-4	0.070	%
		Shrinkage rate	MD:280°C,2.00mm2	ISO 294-4	0.35	%
		Shrinkage rate	Shrinkage rate	MD:120°C,2hr,2.00mm3	ISO 294-4	0.060	%
Water absorption rate	Saturation,23°C	ISO 62	6.5	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	2.3	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	1E+13	ohms
Volume resistivity	23°C	IEC 60093	1E+15	ohms·cm
Dielectric strength	23°C,1.00mm	IEC 60243-1	32	KV/mm
Relative permittivity	23°C,100Hz	IEC 60250	4.50
Relative permittivity	Relative permittivity	23°C,1MHz	IEC 60250	3.90
Dissipation factor	23°C,100Hz	IEC 60250	0.019
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 1
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	195	Mpa
film	Test Condition	Test Method	Test Result	Test Unit
Thin film puncture strength	--6	ISO 6603-2	2.80	J
	Thin film puncture strength	--7	ISO 6603-2	3.40	J
		Thin film puncture strength	--6	ISO 6603-2	791	N
		Thin film puncture strength	Thin film puncture strength	--7	ISO 6603-2	883	N
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut		ISO 1874	PA6.GHR.14-100.GF30

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.