Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 SOLVAY BRAZIL A 205F

Injection grade

US$ 4,380 / MT

FOB Dongguan Port

flammability	Test Condition	Test Method	SOLVAY BRAZIL/A 205F
UL flame retardant rating	0.8mm	UL 94	V-2
Burning wire flammability index	1.6mm	IEC 60695-2-12	850 °C
Extreme Oxygen Index		ISO 4589-2	29 %
UL flame retardant rating	3.2mm	UL 94	V-2
UL flame retardant rating		0.40mm	UL 94	V-2
smoke density		NFF16-101	I3
UL flame retardant rating	1.6mm	UL 94	V-2
UL flame retardant rating			NFF16-101	F2
Physical properties	Test Condition	Test Method	SOLVAY BRAZIL/A 205F
Water absorption rate	23°C,24hr	ISO 62	1.2 %
density		ISO 1183/A	1.14 g/cm³
Supplementary Information	Test Condition	Test Method	SOLVAY BRAZIL/A 205F
EuropeanRailwaysCertifications	R23	EN45545-2	HL2
EuropeanRailwaysCertifications		R22	EN45545-2	HL2
mechanical properties	Test Condition	Test Method	SOLVAY BRAZIL/A 205F
Tensile strain	Yield,23°C	ISO 527-2	4.0 %
tensile strength	Yield,23°C	ASTM D638	85.0 Mpa
Bending modulus	23°C	ASTM D790	3350 Mpa
bending strength	23°C	ISO 178	120 Mpa
Tensile modulus	23°C	ISO 527-2/1A	3200 Mpa
tensile strength	Yield,23°C	ISO 527-2/1A	85.0 Mpa
Bending modulus	23°C	ISO 178	3000 Mpa
tensile strength	Break,23°C	ISO 527-2/1A	60.0 Mpa
bending strength	23°C	ASTM D790	125 Mpa
elongation	Break,23°C	ASTM D638	25 %
Tensile strain	Break,23°C	ISO 527-2	50 %
impact performance	Test Condition	Test Method	SOLVAY BRAZIL/A 205F
Impact strength of cantilever beam gap	23°C	ASTM D256	80 J/m
Impact strength of cantilever beam gap		23°C	ISO 180	5.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.0 kJ/m²
thermal performance	Test Condition	Test Method	SOLVAY BRAZIL/A 205F
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	65.0 °C
		0.45MPa,Unannealed	ISO 75-2/Bf	205 °C
		1.8MPa,Unannealed	ASTM D648	80.0 °C
Melting temperature		ISO 11357-3	263 °C
Electrical performance	Test Condition	Test Method	SOLVAY BRAZIL/A 205F
Dielectric strength	2.00mm	IEC 60243-1	27 KV/mm
Volume resistivity		IEC 60093	1E+15 ohms·cm
Dissipation factor		IEC 60250	0.030
Relative permittivity		IEC 60250	2.90
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Surface resistivity		IEC 60093	5E+15 ohms
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 1