Product Name Manufacturer Model

Brand

Typical Applications

Properties

Color

Form

Processing Methods

Grade

Filler

Recycled Content

Certificates

Reference Price

PC
PC SABIC INNOVATIVE NANSHA 3412ECR-739
Enhanced level
UL
US$ 2,825 / MT
FOB Guangzhou port, China
mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
bending strengthISO 178140 Mpa
Tensile strainBreakISO 527-2/53.2 %
Tensile modulusASTM D6385500 Mpa
bending strengthYield,50.0mmSpanASTM D790156 Mpa
tensile strengthBreakASTM D63887.0 Mpa
YieldISO 527-2/595.0 Mpa
Bending modulusISO 1785500 Mpa
elongationYieldASTM D6383.1 %
Tensile strainYieldISO 527-2/52.8 %
Bending modulus50.0mmSpanASTM D7905000 Mpa
Tensile modulusISO 527-2/16000 Mpa
tensile strengthBreakISO 527-2/590.0 Mpa
YieldASTM D63890.0 Mpa
Physical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
densityISO 11831.36 g/cm³
melt mass-flow rate300°C/1.2kgASTM D12387.0 g/10min
Shrinkage rateTD：3.20mmInternal Method0.20-0.50 %
densityASTM D7921.30 g/cm³
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Shrinkage rateMD：3.20mmInternal Method0.20-0.50 %
Water absorption rateSaturation,23°CISO 620.29 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11337.00 cm3/10min
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Dissipation factor50HzIEC 602500.020
Hot wire ignitionHWIUL 746PLC 0
Relative permittivity50HzIEC 602503.30
Volume resistivityIEC 60093>1.0E+15 ohms·cm
Compared to the anti leakage trace indexCTIUL 746PLC 3
High arc combustion indexHAIUL 746PLC 3
Dissipation factor1MHzIEC 602500.010
60HzIEC 602500.020
Surface resistivityIEC 60093>1.0E+15 ohms
Relative permittivity1MHzIEC 602503.30
60HzIEC 602503.30
High voltage arc tracing rateHVTRUL 746PLC 3
Arc resistanceASTM D495PLC7
flammabilityTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Extreme Oxygen IndexISO 4589-240 %
UL flame retardant rating1.5mmUL 94V-0
Hot filament ignition temperature1.0mmIEC 60695-2-13825 °C
UL flame retardant rating3.0mmUL 945VA
Burning wire flammability index1.0mmIEC 60695-2-12960 °C
thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Linear coefficient of thermal expansionTD：-40to40°CASTME8317E-05 cm/cm/°C
MD：23to80°CISO 11359-23E-05 cm/cm/°C
Ball Pressure Test125°CIEC 60695-10-2Pass
Hot deformation temperature0.45MPa,Unannealed,64.0mmSpanISO 75-2/Bf141 °C
Linear coefficient of thermal expansionTD：23to80°CISO 11359-27E-05 cm/cm/°C
RTI StrUL 746130 °C
Vicat softening temperatureASTM D152510147 °C
Hot deformation temperature1.8MPa,Unannealed,3.20mmASTM D648141 °C
Vicat softening temperature--ISO 306/B50145 °C
Hot deformation temperature1.8MPa,Unannealed,64.0mmSpanISO 75-2/Af136 °C
Linear coefficient of thermal expansionMD：-40to40°CASTME8313E-05 cm/cm/°C
RTI ElecUL 746130 °C
RTI ImpUL 746130 °C
Vicat softening temperature--ISO 306/B120146 °C
impact performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/3412ECR-739
Impact strength of simply supported beam without notch-30°CISO 179/1eU40 kJ/m²
Impact strength of cantilever beam gap-30°CASTM D256110 J/m
Suspended wall beam without notch impact strength23°CISO 180/1U35 kJ/m²
Charpy Notched Impact Strength-30°CISO 179/1eA5.0 kJ/m²
Impact strength of cantilever beam gap23°CASTM D256110 J/m
23°CISO 180/1A7.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU40 kJ/m²
Charpy Notched Impact Strength23°CISO 179/1eA6.0 kJ/m²
Dart impact23°C,TotalEnergyASTM D376320.0 J
Impact strength of cantilever beam gap-30°CISO 180/1A6.0 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U35 kJ/m²