PC
PC COVESTRO THAILAND 3208
Injection grade
US$ 6,322 / MT
FOB Shenzhen Port
optical performanceTest ConditionTest MethodCOVESTRO THAILAND/3208
Refractive indexISO 4891.587
transmissivity3000μmISO 13468-288.0 %
turbidity3000μmISO 14782<0.80 %
transmissivity1000μmISO 13468-289.0 %
4000μmISO 13468-287.0 %
2000μmISO 13468-289.0 %
mechanical propertiesTest ConditionTest MethodCOVESTRO THAILAND/3208
Tensile creep modulus1hrISO 899-12200 Mpa
bending strength23°CISO 17895.0 Mpa
tensile strengthYield,23°CISO 527-2/5065.0 Mpa
Bending strain23°CISO 1787.2 %
Nominal tensile fracture strain23°CISO 527-2/50>50 %
bending strength3.5%Strain,23°CISO 17872.0 Mpa
Tensile creep modulus1000hrISO 899-11900 Mpa
Tensile strainYield,23°CISO 527-2/506.3 %
Break,23°CISO 527-2/50120 %
Bending modulus23°CISO 1782350 Mpa
Tensile modulus23°CISO 527-2/12350 Mpa
tensile strengthBreak,23°CISO 527-2/5075.0 Mpa
hardnessTest ConditionTest MethodCOVESTRO THAILAND/3208
Ball Pressure TestISO 2039-1111 Mpa
impact performanceTest ConditionTest MethodCOVESTRO THAILAND/3208
Charpy Notched Impact Strength23°C,Partial BreakISO 739180 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eUNoBreak
Charpy Notched Impact Strength-30°C,Complete BreakISO 739118 kJ/m²
Impact strength of simply supported beam without notch-60°CISO 179/1eUNoBreak
Multi axis Instrumented Impact Energy23°CISO 6603-265.0 J
Multi axis Instrumented Peak Impact Force23°CISO 6603-25800 N
Impact strength of simply supported beam without notch23°CISO 179/1eUNoBreak
Impact strength of cantilever beam gap-30°C,Complete BreakISO 739120 kJ/m²
Multi axis Instrumented Peak Impact Force-30°CISO 6603-26700 N
Multi axis Instrumented Impact Energy-30°CISO 6603-275.0 J
Impact strength of cantilever beam gap23°C,Partial BreakISO 739175 kJ/m²
Physical propertiesTest ConditionTest MethodCOVESTRO THAILAND/3208
melt mass-flow rate300°C/1.2kgISO 11335.5 g/10min
Shrinkage rateMDISO 25770.60-0.80 %
TD:2.00mm3ISO 294-40.75 %
Apparent densityISO 600.66 g/cm³
Shrinkage rateMD:2.00mm3ISO 294-40.70 %
TDISO 25770.60-0.80 %
density23°CISO 11831.20 g/cm³
Water absorption rateEquilibrium,23°C,50%RHISO 620.12 %
Saturation,23°CISO 620.30 %
Melt Volume Flow Rate (MVR)300°C/1.2kgISO 11335.00 cm3/10min
flammabilityTest ConditionTest MethodCOVESTRO THAILAND/3208
FlashIgnitionTemperatureASTM D1929480 °C
SelfIgnitionASTM D1929550 °C
thermal performanceTest ConditionTest MethodCOVESTRO THAILAND/3208
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A130 °C
Vicat softening temperature--ISO 306/B50150 °C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-26.5E-05 cm/cm/°C
Ball Pressure Test141°CIEC 60695-10-2Pass
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B142 °C
Glass transition temperatureISO 11357-2150 °C
Vicat softening temperature--ISO 306/B120151 °C
thermal conductivity23°CISO 83020.20 W/m/K
Linear coefficient of thermal expansionMD：23to55°CISO 11359-26.5E-05 cm/cm/°C