PC/ABS CY8630-701 PC/ABS vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Reference Price

PC/ABS SABIC INNOVATIVE NANSHA CY8630-701

Injection grade

US$ 2,830 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CY8630-701
bending strength	--5,6	ISO 178	85.0 Mpa
bending strength		Yield,50.0mmSpan4	ASTM D790	87.0 Mpa
elongation	Yield3	ASTM D638	5.3 %
		Yield	ISO 527-2/50	5.2 %
		Break3	ASTM D638	75 %
tensile strength	Break	ISO 527-2/50	55.0 Mpa
		Yield	ISO 527-2/50	58.0 Mpa
		Yield3	ASTM D638	58.0 Mpa
Tensile modulus	--2	ASTM D638	2250 Mpa
Bending modulus	50.0mmSpan4	ASTM D790	2300 Mpa
Tensile modulus	--	ISO 527-2/1	2250 Mpa
Bending modulus	--5	ISO 178	2300 Mpa
elongation	Break	ISO 527-2/50	75 %
tensile strength	Break3	ASTM D638	50.0 Mpa
thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CY8630-701
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	110 °C
Ball Pressure Test	100°C10	IEC 60695-10-2	通过
Ball Pressure Test		75°C	IEC 60695-10-2	通过
Vicat softening temperature	--	ISO 306/B120	133 °C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7E-05 cm/cm/°C
Linear coefficient of thermal expansion		TD:-40to40°C	ASTME831	8E-05 cm/cm/°C
Vicat softening temperature	--	ASTM D15259	131 °C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	128 °C
Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CY8630-701
Water absorption rate	23°C,24hr	ISO 62	0.30 %
Shrinkage rate	MD:3.20mm	Internal Method	0.50-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20 %
Water absorption rate		Saturation,23°C	ISO 62	0.60 %
Shrinkage rate	TD:3.20mm	Internal Method	0.50-0.70 %
impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CY8630-701
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	25 kJ/m²
Dart impact	-30°C,TotalEnergy	ASTM D3763	90.0 J
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	无断裂
Charpy Notched Impact Strength	23°C	ISO 179/1eA	50 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	90.0 J
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	无断裂
Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/CY8630-701
Volume resistivity		IEC 60093	>1.0E+16 ohms·cm