PC/ABS CY8630-701 SABIC INNOVATIVE NANSHA

105

Form：Granules | Grade：Injection grade

Properties:

High temperature resistanHigh mobility

Typical Applications:

Electrical applicationsHome appliance componentsApplication in the automotive field

Supplier(2)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical applications \| Home appliance components \| Application in the automotive field
Properties:	High temperature resistan \| High mobility

Certificates

No Data...

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	25	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	50	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂
Dart impact	-30°C,TotalEnergy	ASTM D3763	90.0	J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	90.0	J
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	--2	ASTM D638	2250	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2250	Mpa
tensile strength	Yield3	ASTM D638	58.0	Mpa
	tensile strength	Yield	ISO 527-2/50	58.0	Mpa
		tensile strength	Break3	ASTM D638	50.0	Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	55.0	Mpa
elongation	Yield3	ASTM D638	5.3	%
	elongation	Yield	ISO 527-2/50	5.2	%
		elongation	Break3	ASTM D638	75	%
		elongation	elongation	Break	ISO 527-2/50	75	%
Bending modulus	50.0mmSpan4	ASTM D790	2300	Mpa
Bending modulus	Bending modulus	--5	ISO 178	2300	Mpa
bending strength	--5,6	ISO 178	85.0	Mpa
bending strength	bending strength	Yield,50.0mmSpan4	ASTM D790	87.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	128	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	110	°C
Vicat softening temperature	--	ASTM D15259	131	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	133	°C
Ball Pressure Test	75°C	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	100°C10	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	7E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	TD:3.20mm	Internal Method	0.50-0.70	%
Water absorption rate	23°C,24hr	ISO 62	0.30	%
	Water absorption rate	Saturation,23°C	ISO 62	0.60	%
	Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Shrinkage rate	MD:3.20mm	Internal Method	0.50-0.70	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		IEC 60093	>1.0E+16	ohms·cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top