PA66 TORAY JAPAN CM3004G30

Enhanced level

US$ 5,250 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	TORAY JAPAN/CM3004G30
bending strength	23°C		250 MPa
Bending modulus	23°C	MPa	9300 6500
Tensile strain	Break,80°C	%	4.5 --
Tensile strain		Break,23°C	%	3.0 3.0
Bending modulus	-40°C	MPa	10200 --
Bending modulus		23℃	ASTM D-790	无水｜93200 kg/cm2
tensile strength	23°C		165 MPa
Bending modulus	80°C	MPa	5500 --
Impact strength of cantilever beam gap	23℃，Unnotched1/8		无水｜65 kg.cm/cm
tensile strength	80°C	MPa	110 --
bending strength	80°C	MPa	150 --
bending strength		23℃	ASTM D-790	无水｜2490 kg/cm2
tensile strength	-40°C	MPa	190 --
Elongation at Break	23℃	ASTM D-638	无水｜5 %
Tensile strain	Break,-40°C	%	2.5 --
tensile strength	23℃，Break	ASTM D-638	无水｜1640 kg/cm2
Taber abraser	1000Cycles	mg	26.0 --
bending strength	-40°C	MPa	275 --
Electrical performance	Test Condition	Test Method	TORAY JAPAN/CM3004G30
Arc resistance	1/8"	ASTM D-495	无水｜70-80 S
Dielectric constant	23°C,1MHz		0.0100 --
Arc resistance		sec	70.0 --
Volume resistivity		ASTM D-257	1.3%水｜8×1013 Ω.cm
Dielectric strength		kV/mm	38 33
Compared to the anti leakage trace index	CTI	V	PLC 3
Dielectric constant	23°C,1kHz		4.00 --
Dissipation factor	106Hz	ASTM D-150	无水｜0.003-0.009
Dielectric strength	1/8"	ASTM D-149	无水｜38 KV/mm
Volume resistivity		ohms·cm	1E+15 1E+13
Compared to the Leakage Traceability Index (CTI)		UL 746	无水｜200 V
Physical properties	Test Condition	Test Method	TORAY JAPAN/CM3004G30
Water absorption rate	23°C,24hr	%	0.60 --
density		ASTM D-792	无水｜1.59
Shrinkage rate	TD:3.00mm3	%	0.60-0.90 --
Shrinkage rate		MD:3.00mm4	%	0.20-0.50 --
density	23°C	g/cm³	1.59 --
Water absorption rate	Saturation,23°C	%	4.0 --
hardness	Test Condition	Test Method	TORAY JAPAN/CM3004G30
Rockwell hardness	R-Sale,23°C		121 --
thermal performance	Test Condition	Test Method	TORAY JAPAN/CM3004G30
UL-94 flame retardant grade		UL 94	1.3%水｜-
Melting temperature		°C	265 --
Hot deformation temperature	0.45MPa,Unannealed	°C	251 --
Hot deformation temperature		18.6kg/cm2	ASTM D-648	1.3%水｜- °C
Melting temperature		差示扫描测热计DSC法	265 °C
Linear coefficient of thermal expansion	MD	cm/cm/°C	2E-05 --
Linear coefficient of thermal expansion			ASTM D-696	1.3%水｜- 10-5cm/cm.℃
impact performance	Test Condition	Test Method	TORAY JAPAN/CM3004G30
Charpy Notched Impact Strength	-40°C	kJ/m²	7.0 --
Impact strength of simply supported beam without notch	23°C	kJ/m²	65 70
Charpy Notched Impact Strength	23°C	kJ/m²	9.5 14
Other performance	Test Condition	Test Method	TORAY JAPAN/CM3004G30
filler content			1.3%水｜- wt%
Basic Performance	Test Condition	Test Method	TORAY JAPAN/CM3004G30
Water absorption rate	23℃，24hr	ASTM D-570	无水｜0.4 %
flammability	Test Condition	Test Method	TORAY JAPAN/CM3004G30
UL flame retardant rating	0.40mm		V-0 --