PA66 CM3004G30 TORAY JAPAN

Form：Granules | Grade：Enhanced level

Properties:

Flame retardantGlass fiber reinforced Glass fiber reinforced bFiller: Glass fiber reinfFlame retardant grade30% filler by weighthalogen-containing

Typical Applications:

Electrical fieldElectronic fieldbuilding materialsAutomotive sectorOffice supplies

Supplier(1)

Product Description

Certificates(0)

Datasheet

Product Description

Typical Applications:	Electrical field \| Electronic field \| building materials \| Automotive sector \| Office supplies
Properties:	Flame retardant \| Glass fiber reinforced \| Glass fiber reinforced b \| Filler: Glass fiber reinf \| Flame retardant grade \| 30% filler by weight \| halogen-containing

Certificates

No Data...

Technical Data Sheet

Other performance	Test Condition	Test Method	Test Result	Test Unit
filler content			无水｜30	wt%
filler content	filler content			1.3%水｜-	wt%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-40°C	kJ/m²	7.0	--
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	kJ/m²	9.5	14
Impact strength of simply supported beam without notch	23°C	kJ/m²	65	70
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.40mm		V-0	--
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	23℃，24hr	ASTM D-570	1.3%水｜-	%
Water absorption rate	Water absorption rate	23℃，24hr	ASTM D-570	无水｜0.4	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus	23℃	ASTM D-790	1.3%水｜65000	kg/cm2
Bending modulus	Bending modulus	23℃	ASTM D-790	无水｜93200	kg/cm2
bending strength	23℃	ASTM D-790	1.3%水｜2000	kg/cm2
bending strength	bending strength	23℃	ASTM D-790	无水｜2490	kg/cm2
Elongation at Break	23℃	ASTM D-638	1.3%水｜5	%
Elongation at Break	Elongation at Break	23℃	ASTM D-638	无水｜5	%
tensile strength	23℃，Break	ASTM D-638	1.3%水｜1350	kg/cm2
tensile strength	tensile strength	23℃，Break	ASTM D-638	无水｜1640	kg/cm2
Impact strength of cantilever beam gap	23℃，Unnotched1/8		1.3%水｜70	kg.cm/cm
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃，Unnotched1/8		无水｜65	kg.cm/cm
Tensile strain	Break,-40°C	%	2.5	--
	Tensile strain	Break,23°C	%	3.0	3.0
	Tensile strain	Tensile strain	Break,80°C	%	4.5	--
Bending modulus	-40°C	MPa	10200	--
	Bending modulus	23°C	MPa	9300	6500
	Bending modulus	Bending modulus	80°C	MPa	5500	--
bending strength	-40°C	MPa	275	--
	bending strength	23°C		250	MPa
	bending strength	bending strength	80°C	MPa	150	--
Taber abraser	1000Cycles	mg	26.0	--
tensile strength	-40°C	MPa	190	--
	tensile strength	23°C		165	MPa
	tensile strength	tensile strength	80°C	MPa	110	--
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion		ASTM D-696	无水｜2	10-5cm/cm.℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D-696	1.3%水｜-
Hot deformation temperature	18.6kg/cm2	ASTM D-648	无水｜251	°C
Hot deformation temperature	Hot deformation temperature	18.6kg/cm2	ASTM D-648	1.3%水｜-	°C
Melting temperature		差示扫描测热计DSC法	265	°C
UL-94 flame retardant grade		UL 94	无水｜V-0
UL-94 flame retardant grade	UL-94 flame retardant grade		UL 94	1.3%水｜-
Hot deformation temperature	0.45MPa,Unannealed	°C	251	--
Melting temperature		°C	265	--
Linear coefficient of thermal expansion	MD	cm/cm/°C	2E-05	--
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ASTM D-792	1.3%水｜-
	density		ASTM D-792	无水｜1.59
	density	density	23°C	g/cm³	1.59	--
Shrinkage rate	TD:3.00mm3	%	0.60-0.90	--
Shrinkage rate	Shrinkage rate	MD:3.00mm4	%	0.20-0.50	--
Water absorption rate	23°C,24hr	%	0.60	--
Water absorption rate	Water absorption rate	Saturation,23°C	%	4.0	--
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity		ASTM D-257	无水｜8×1014	Ω.cm
Arc resistance	1/8"	ASTM D-495	1.3%水｜-	S
Arc resistance	Arc resistance	1/8"	ASTM D-495	无水｜70-80	S
Dissipation factor	106Hz	ASTM D-150	1.3%水｜-
Dissipation factor	Dissipation factor	106Hz	ASTM D-150	无水｜0.003-0.009
Compared to the Leakage Traceability Index (CTI)		UL 746	1.3%水｜-	V
Compared to the Leakage Traceability Index (CTI)	Compared to the Leakage Traceability Index (CTI)		UL 746	无水｜200	V
Dielectric strength	1/8"	ASTM D-149	1.3%水｜33	KV/mm
Dielectric strength	Dielectric strength	1/8"	ASTM D-149	无水｜38	KV/mm
Volume resistivity		ASTM D-257	1.3%水｜8×1013	Ω.cm
Dielectric strength		kV/mm	38	33
Dielectric constant	23°C,1kHz		4.00	--
Dielectric constant	Dielectric constant	23°C,1MHz		0.0100	--
Volume resistivity		ohms·cm	1E+15	1E+13
Arc resistance		sec	70.0	--
Compared to the anti leakage trace index	CTI	V	PLC 3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Sale,23°C		121	--

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.