PBT SK601 BK851 PBT vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PBT DUPONT USA SK601 BK851

Enhanced level

US$ 3,150 / MT

FOB Guangzhou port, China

mechanical properties	Test Condition	Test Method	DUPONT USA/SK601 BK851
bending strength		ISO 178	140 Mpa
bending strength		0.00 mm, 23 ℃, 0.0 %	ISO 178	140 MPa
Tensile strain	Break	ISO 527-2	4.0 %
tensile strength	Break	ISO 527-2	90.0 Mpa
Tensile modulus		ISO 527-2	4500 Mpa
bending strength		ASTM D790/ISO 178	140 kg/cm²(MPa)[Lb/in²]
Tensile modulus	0.00 mm, 23℃, Injection Molded	ISO 527-1	4500 MPa
Elongation at Break		ASTM D638/ISO 527	4 %
Supplementary Information	Test Condition	Test Method	DUPONT USA/SK601 BK851
EmissionofOrganicCompounds		VDA277	72.0 µgC/g
Odor		VDA270	3.00
Physical properties	Test Condition	Test Method	DUPONT USA/SK601 BK851
Water absorption rate		ASTM D570/ISO 62	0.2 %
Shrinkage rate		ASTM D955	1.2 %
Top out temperature			170 °C
density		ASTM D792/ISO 1183	1370
flammability	Test Condition	Test Method	DUPONT USA/SK601 BK851
UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	20 %
Burning rate	1.00mm	ISO 3795	36 mm/min
UL flame retardant rating	3.0mm	UL 94	HB
		3.0mm	IEC 60695-11-10,-20	HB
		1.5mm	UL 94	HB
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	1E-04 g
thermal performance	Test Condition	Test Method	DUPONT USA/SK601 BK851
Hot deformation temperature	HDT	ASTM D648/ISO 75	180 ℃（℉）
UL flame retardant rating	3.00 mm	UL 94	HB
UL flame retardant rating		1.50 mm	UL 94	HB
Combustibility (rate)		UL 94	HB
Melting temperature			225 ℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	180 °C
UL flame retardant rating	6.00 mm	UL 94	HB
Melting temperature		ISO 11357-3	225 °C
other	Test Condition	Test Method	DUPONT USA/SK601 BK851
characteristic			10%玻纤增强.润滑.注射成型
impact performance	Test Condition	Test Method	DUPONT USA/SK601 BK851
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35 kJ/m²
Impact strength of simply supported beam without notch		-30°C	ISO 179/1eU	35 kJ/m²
Electrical performance	Test Condition	Test Method	DUPONT USA/SK601 BK851
Compared to the anti leakage trace index		IEC 60112	PLC 2