PBT SK601 BK851 DUPONT USA

Form：Granules | Grade：Enhanced level

Properties:

Glass fiber reinforced

Typical Applications:

Automotive ApplicationsElectronic and electrical components

Supplier(1)

Product Description

Certificates(1)

Datasheet

Product Description

Typical Applications:	Automotive Applications \| Electronic and electrical components
Properties:	Glass fiber reinforced

Certificates

Technical Data Sheet

other	Test Condition	Test Method	Test Result	Test Unit
characteristic			10%玻纤增强.润滑.注射成型
impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	35	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	35	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Burning rate	1.00mm	ISO 3795	36	mm/min
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	20	%
FMVSS flammability		FMVSS302	B
Fogging-G-value	condensate	ISO 6452	1E-04	g
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus	0.00 mm, 23℃, Injection Molded	ISO 527-1	4500	MPa
bending strength	0.00 mm, 23 ℃, 0.0 %	ISO 178	140	MPa
Tensile modulus		ISO 527-2	4500	Mpa
tensile strength	Break	ISO 527-2	90.0	Mpa
Tensile strain	Break	ISO 527-2	4.0	%
bending strength		ISO 178	140	Mpa
Elongation at Break		ASTM D638/ISO 527	4	%
bending strength		ASTM D790/ISO 178	140	kg/cm²(MPa)[Lb/in²]
thermal performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	6.00 mm	UL 94	HB
	UL flame retardant rating	3.00 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	1.50 mm	UL 94	HB
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	180	°C
Melting temperature		ISO 11357-3	225	°C
Combustibility (rate)		UL 94	HB
Hot deformation temperature	HDT	ASTM D648/ISO 75	180	℃（℉）
Melting temperature			225	℃（℉）
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Top out temperature			170	°C
density		ASTM D792/ISO 1183	1370
Shrinkage rate		ASTM D955	1.2	%
Water absorption rate		ASTM D570/ISO 62	0.2	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112	PLC 2
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
EmissionofOrganicCompounds		VDA277	72.0	µgC/g
Odor		VDA270	3.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.