PA66 A30SFN31 PA66 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA66 LANXESS GERMANY A30SFN31

Flame retardant grade

US$ 4,560 / MT

FOB Guangzhou port, China

Electrical performance	Test Condition	Test Method	LANXESS GERMANY/A30SFN31
Dissipation factor	23℃，1 MHz23°C, 1 MHz	IEC 60250	0.019
Dielectric strength	23 ℃，1 mm23℃，1.00 mm	IEC 60243-1	30 KV/mm
Relative permittivity	23℃，1 MHz23°C, 1 MHz	IEC 60250	4
Volume resistivity	23℃23℃	IEC 60093	100000000000000 ohms·cm
Compared to the anti leakage trace index	Solution ASolution A	IEC 60112	PLC 0
Relative permittivity	23℃，100 Hz23°C, 100 Hz	IEC 60250	4
Surface resistivity		IEC 60093	1000000000000000 ohms
Dissipation factor	23℃，100 Hz23°C, 100 Hz	IEC 60250	0.012
thermal performance	Test Condition	Test Method	LANXESS GERMANY/A30SFN31
Vicat softening temperature	B120B120	ISO 306/B120	230 °C
Linear coefficient of thermal expansion	TD：23~55℃TD：23 to 55℃	ISO 11359-2	0.000070 1/℃
Linear coefficient of thermal expansion		MD：23~55℃MD：23 to 55℃	ISO 11359-2	0.000080 1/℃
Melting temperature		ISO 11357-3	265 °C
impact performance	Test Condition	Test Method	LANXESS GERMANY/A30SFN31
Suspended wall beam without notch impact strength	-30℃-30°C	ISO 180/1U	55 kJ/m²
Impact strength of cantilever beam gap	23℃23℃	ISO 180-1A	< 10 kJ/m²
Suspended wall beam without notch impact strength	23℃23°C	ISO 180/1U	55 kJ/m²
Impact strength of simply supported beam without notch	23℃23°C	ISO 179/1eU	60 kJ/m²
Impact strength of simply supported beam without notch		-30℃-30°C	ISO 179/1eU	50 kJ/m²
flame retardant performance	Test Condition	Test Method	LANXESS GERMANY/A30SFN31
Ultimate Oxygen Index		ISO 4589-2	34 %
0.40 mm??0.40 mm	0.40mm	UL 94	V-0
Glow wire combustion index (GWFI)	0.40 mm0.40 mm	IEC 60695-2-12	960 °C
Ignition temperature of heating wire	0.4 mm0.40 mm	IEC 60695-2-13	775 °C
mechanical properties	Test Condition	Test Method	LANXESS GERMANY/A30SFN31
Tensile modulus	23℃23℃	ISO 527-1-2	3800 Mpa
Bending strain	23°C		5.8 %
bending strength	3.50% Strain3.5% Strain	ISO 178-A	120 Mpa
tensile strength	Yield，23℃Yield，23℃	ISO 527-2/50	85 Mpa
Bending modulus	23℃23℃4	ISO 178-A	3700 Mpa
bending strength	23℃23°C	ISO 178	125 Mpa
Tensile strain	Yield，23℃Yield，23℃	ISO 527-2/50	4.1 %
Physical properties	Test Condition	Test Method	LANXESS GERMANY/A30SFN31
Shrinkage rate	MD：120℃，2.0 mm，2 hrsFlow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.1 %
		TD：270℃，2.0 mmAcross Flow : 518°F, 0.0787 in 22	ISO 294-4	1.1 %
		TD：120℃，2.0 mm，2 hrsAcross Flow : 120°C, 2 hr, 2.00 mm 33	ISO 294-4	0.1 %
density	23°C	ISO 1183	1.17 g/cm³
Shrinkage rate	MD：270℃，2.0 mmFlow : 518°F, 0.0787 in 22	ISO 294-4	1.1 %